EAA 1430真货原厂产地 盛禧奥(斯泰隆) EAA1430物性表
物理性能测试条件测试方法测试结果单位密度 / 比重g/cm³ASTM D-7920.93
g/cm³ISO 11830.93
ASTMD792,ISO11830.930g/cm³熔体质量流动速率2190°C/2.16kgASTMD1238,ISO11335.0g/10min共聚单体含量3
内部方法9.7%机械性能测试条件测试方法测试结果单位抗张强度屈服,模压成型4ASTMD6387.67Mpa屈服,模压成型ISO527-2/5087.67Mpa断裂,模压成型4ASTMD63819.5Mpa断裂,模压成型ISO527-2/50819.5Mpa伸长率断裂,模压成型4ASTMD638580%断裂,模压成型ISO527-2/508580%拉伸屈服强度Compression MoldedMPaASTM D-6387.67Compression MoldedMPaISO 527-2/5087.67拉伸断裂强度Compression MoldedMPaASTM D-63819.5Compression MoldedMPaISO 527-2/50819.5拉伸断裂伸长率Compression Molded%ASTM D-638580Compression Molded%ISO 527-2/508580薄膜厚度-Tested
um
50.8拉伸屈服强度(MD)50.8umMPaASTM D-88210.4拉伸屈服强度(TD)50.8umMPaASTM D-88210.2拉伸屈服强度(MD)50.8umMPaISO 527-310.4拉伸屈服强度(TD)50.8umMPaISO 527-310.2拉伸断裂强度(TD)50.8umMPaASTM D-88231.0拉伸断裂强度(MD)50.8umMPaASTM D-88230.6拉伸断裂强度(TD)50.8umMPaISO 527-331拉伸断裂强度(MD)50.8umMPaISO 527-330.6拉伸断裂伸长率(MD)50.8um%ASTM D-882420拉伸断裂伸长率(TD)50.8um%ASTM D-88247050.8um%ISO 527-3470拉伸断裂伸长率(MD)50.8um%ISO 527-3420埃尔曼多夫撕裂强度(MD)50.8umgASTM D-1922470埃尔曼多夫撕裂强度(TD)50.8umgASTM D-1922730埃尔曼多夫撕裂强度(MD)50.8umNISO 6383-22100埃尔曼多夫撕裂强度(TD)50.8umNISO 6383-23300光学性能测试条件测试方法测试结果单位光泽度45°，50.8um
ASTM D-245774雾度（Haze）50.8um%ISO 14782450.8um%ASTM D-10034熔体温度
℃
196光泽度45°,50.8µmASTMD245774
雾度（Haze）50.8µmASTMD10034.0%50.8µmISO147824.0%热性能测试条件测试方法测试结果单位维卡软化温度
ASTMD1525,ISO30676.1°C溶融温度（DSC）
内部方法96.1°C维卡软化点
℃ASTM D-152576.1
℃ISO 30676.1熔融温度
℃Internal Method96.1薄膜测试条件测试方法测试结果单位埃尔曼多夫抗撕强度5MD:51µmASTMD1922470gTD:51µmASTMD1922730gMD:51µmISO6383-22100NTD:51µmISO6383-23300N抗张强度MD:屈服,51µmASTMD88210.4MpaTD:屈服,51µmASTMD88210.2MpaMD:屈服,51µmISO527-310.4MpaTD:屈服,51µmISO527-310.2MpaMD:断裂,51µmASTMD882,ISO527-330.6MpaTD:断裂,51µmASTMD882,ISO527-331.0Mpa伸长率MD:断裂,51µmASTMD882,ISO527-3420%TD:断裂,51µmASTMD882,ISO527-3470%基本性能测试条件测试方法测试结果单位熔体流动速率190℃/2.16kgg/10minASTM D-12385190℃/2.16kgg/10minISO 11335单体含量
%Internal Method9.7