Generic Name: 聚偏二氟乙烯 (PVDF) - 提供方: Arkema High Performance Polymers
Kynar Flex® resins are fluorinated thermoplastic copolymers.
Kynar Flex® 3120-50 is a pelletized flexible, semi-crystalline VF2 based copolymer. It can be molded or extruded and has a useful temperature range from -40°C - 150°C. Kynar Flex® 3120-50 has a UL RTI of 150°C.
Kynar Flex® 3120-50 can be used in compounding for cross-linkable wire and cable as well as both wire applications requiring low temperature flexibility and high temperature resistance.
Kynar Flex® 3120-50 also finds use as a polymer processing aid (PPA) for polyolefins. The use of Kynar Flex® 3120-50 or Kynar Flex 3121-50 at 200 -1000 ppm levels reduces extruder pressure, improves surface finish, reduces die build up, and improves gauge control.
与典型值比较 - Upgrade to compare! 与黄卡比较
单位: SI
总览
材料状态
已商用：当前有效
资料 1Technical Datasheet (English)
UL 黄卡 2E54699-534488
搜索 UL 黄卡Arkema High Performance Polymers
供货地区北美洲
非洲和中东
拉丁美洲
欧洲
亚太地区
添加剂热稳定剂
紫外线稳定剂
特性半结晶
低温下的柔性
共聚物
光稳定
可交联
良好的柔韧性
耐热性，高
热稳定性
用途电线电缆应用
混料
塑料改性
形式粒子
加工方法复合
挤出
型材挤出成型
注射成型
物理性能额定值
单位制
测试方法
密度 / 比重-- 4
1.75 到 1.77
g/cm³
ASTM D792--1.78
g/cm³
ISO 1183熔流率（熔体流动速率） (230°C/12.5 kg)2.5 到 7.5
g/10 min
ASTM D1238熔融体积流量（MVR） (230°C/10.0 kg)0.50
cm³/10min
ISO 1133吸水率饱和
0.030 到 0.050
%
ASTM D570饱和, 23°C0.030
%
ISO 62机械性能额定值
单位制
测试方法
拉伸模量23°C
689 到 1170
MPa
ASTM D638--700
MPa
ISO 527-1抗张强度屈服, 23°C
24.1 到 34.5
MPa
ASTM D638屈服27.0
MPa
ISO 527-2断裂, 23°C34.5 到 48.3
MPa
ASTM D638伸长率屈服, 23°C
10 到 20
%
ASTM D638屈服15
%
ISO 527-2断裂, 23°C300 到 500
%
ASTM D638标称拉伸断裂应变> 50
%
ISO 527-2弯曲模量 (23°C)621 到 827
MPa
ASTM D790弯曲强度 (5.0% 应变, 23°C)20.7 到 34.5
MPa
ASTM D790压缩强度 (23°C)31.0 到 41.4
MPa
ASTM D695摩擦系数 4ASTM D1894与钢 - 动态
0.30
与钢 - 静态
0.31
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
16.0 到 19.0
mg
内部方法冲击性能额定值
单位制
测试方法
简支梁缺口冲击强度 (23°C)无断裂
ISO 179/1eA悬壁梁缺口冲击强度 (23°C)
无断裂
ASTM D256无缺口悬臂梁冲击 (23°C)
无断裂
ASTM D256硬度
额定值
单位制
测试方法
肖氏硬度 (邵氏 D, 23°C)65 到 70
ASTM D2240热性能
额定值
单位制
测试方法
载荷下热变形温度0.45 MPa, 未退火 5
54.4 到 76.7
°C
ASTM D6481.8 MPa, 未退火 543.3 到 54.4
°C
ASTM D6481.8 MPa, 未退火50.0
°C
ISO 75-2/A玻璃转化温度--
-41.1 到 -39.4
°C
ASTM D7028-- 6-40.0
°C
ISO 11357-2熔融温度-- 6
165
°C
ISO 11357-3--161 到 168
°C
ASTM D3418线形热膨胀系数 - 流动 (23°C)1.3E-4 到 1.9E-4
cm/cm/°C
ASTM D696比热745 到 958
J/kg/°C
DSC导热系数0.14 到 0.18
W/m/K
ASTM D433RTI Elec150
°C
UL 746BRTI Imp150
°C
UL 746BRTI150
°C
UL 746B电气性能额定值
单位制
测试方法
表面电阻率 (23°C)5.3E+11 到 5.5E+11
ohms
ASTM D257介电强度 (23°C)51 到 59
kV/mm
ASTM D149介电常数 (1 kHz)3.20 到 10.2
ASTM D150耗散因数 (100 kHz)
0.020 到 0.19
ASTM D150可燃性
额定值
单位制
测试方法
可燃性等级IEC 60695-11-10, -201.0 mm
V-0
5VA
1.5 mm
V-0
极限氧指数
-- 4
42
%
ASTM D2863--43
%
ISO 4589-2光学性能额定值
单位制
测试方法
折射率 71.410
ASTM D542充模分析
额定值
单位制
测试方法
熔体粘度 (230°C, 100 sec^-1)2000 到 2600
Pa·s
ASTM D3835补充信息额定值
单位制
测试方法
热分解温度TGAin air, 1% wt. loss
375
°C
in nitrogen, 1% wt. loss
410
°C