热稳定 低翘曲 PA6 德国巴斯夫 8262GHS BK125 矿物填充 外壳 轴承 汽车领域

热稳定 低翘曲 PA6 德国巴斯夫 8262GHS BK125 矿物填充 外壳 轴承 汽车领域Ultramid® 8262G HS BK-125Polyamide 6BASF Corporation20% 玻璃矿物产品说明：Ultramid 8262G HS BK-125 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation.ApplicationsUltramid 8262G HS BK-125 is generally recommended for applications such as automotive housings, brackets, hubs, shrouds and roller bearings物性信息：基本信息填料/增强材料玻璃\矿物, 20% 填料按重量添加剂热稳定剂特性尺寸稳定性良好低翘曲性热稳定性用途汽车领域的应用外壳轴承机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规外观黑色形式粒子加工方法注射成型物理性能额定值单位制测试方法比重1.29g/cm³ASTM D792, ISO 1183收缩率 - 流动 (3.18 mm)0.80%吸水率    24 hr1.3%ASTM D570    23°C, 24 hr1.3%ISO 62    饱和7.9%ASTM D570    饱和, 23°C7.9%ISO 62    平衡, 50% RH2.2%ASTM D570    平衡, 23°C, 50% RH2.2%ISO 62机械性能额定值单位制测试方法拉伸模量 (23°C)5300MPaISO 527-2抗张强度 (断裂, 23°C)100MPaASTM D638, ISO 527-2伸长率 (断裂, 23°C)3.5%ASTM D638, ISO 527-2弯曲模量 (23°C)4600MPaASTM D790, ISO 178弯曲强度 (23°C)160MPaASTM D790, ISO 178冲击性能额定值单位制测试方法简支梁缺口冲击强度ISO 179    -30°C3.0kJ/m²ISO 179    23°C3.3kJ/m²ISO 179悬壁梁缺口冲击强度    23°C35J/mASTM D256    -40°C3.0kJ/m²ISO 180    23°C4.0kJ/m²ISO 180热性能额定值单位制测试方法热变形温度    0.45 MPa, 未退火211°CISO 75-2/B    1.8 MPa, 未退火185°CASTM D648    1.8 MPa, 未退火163°CISO 75-2/A熔融峰值温度220°CASTM D3418, ISO 3146注射额定值单位制干燥温度83.0°C干燥时间2.0 到 4.0hr建议的最大水分含量0.15%加工（熔体）温度270 到 295°C模具温度80.0 到 95.0°C注塑压力3.45 到 10.3MPa注射速度快速热稳定 低翘曲 PA6 德国巴斯夫 8262GHS BK125 矿物填充 外壳 轴承 汽车领域