ABS 920(Toyolac® 920 555)透明

ABS 920(Toyolac® 920 555)透明ABS 920(Toyolac® 920 555)透明物性性能测试条件测试方法测试结果单位熔融指数（流动系数）ASTM D1238/ISO 113325g/10min密度ASTM D792/ISO 11831.09物理性能测试条件测试方法测试结果单位熔融指数220℃/10kgISO 113325g/10min吸水性浸入23℃水中24小时ASTM D-5700.3%熔融指数220℃ 10kgASTM D-123819～23g/10min燃烧性UL-9494HB熔融粘度220℃3.5～5.0机械性能测试条件测试方法测试结果单位屈服强度23℃ASTM D-638490kg/cm洛氏硬度23℃ASTM D-785115R屈服下的拉伸23℃ASTM D-6383.5%断裂强度下的拉伸23℃ASTM D-63830%挠曲极限23℃ASTM D-79023500kg/cm冲击强度12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ASTM D-2569；7；6kg.cm/cm3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ASTM D-25610；7；6kg.cm/cm挠曲强度23℃ASTM D-790780kg/cm断裂强度23℃ASTM D-638380kg/cm拉伸屈服应力23℃ISO 527-254.0Mpa拉伸断裂应变23℃ISO 527-217%断裂伸长率ASTM D638/ISO 52720%拉伸强度ASTM D638/ISO 52748kg/cm²(MPa)[Lb/in²]洛氏硬度ASTM D785115弯曲模量ASTM D790/ISO 1782160kg/cm²(MPa)[Lb/in²]弯曲强度ASTM D790/ISO 17874kg/cm²(MPa)[Lb/in²]IZOD 缺口冲击强度ASTM D256/ISO 179108kg·cm/cm(J/M)ft·lb/in热性能测试条件测试方法测试结果单位燃烧性（率）UL94HB热变形温度ASTM D648/ISO 7583℃（℉）线性膨胀系数ASTM D-6961.2×10mm/mm/℃热变形温度18.56kg/cmASTM D-64889°C1.8MPa，未退火ISO 75-2/A77.0°CUL阻燃等级UL 94HB