加纤34% PA6 德国巴斯夫 TG7S 冲击改性 热稳定 草坪 园林设备 坐椅

加纤34% PA6 德国巴斯夫 TG7S 冲击改性 热稳定 草坪 园林设备 坐椅 Ultramid® TG7SPolyamide 6BASF Corporation34% 玻璃纤维增强材料产品说明：Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI.ApplicationsInclude cushion seat pan/frame and other automotive seating applications, automotive fan, power tools and trimmer components.物性信息：基本信息黄卡编号E36632-231205填料/增强材料玻璃纤维增强材料, 34% 填料按重量添加剂冲击改性剂热稳定剂特性冲击改性刚性，良好抗撞击性，良好良好的强度热稳定性用途草坪和园林设备动力/其它工具汽车领域的应用座椅机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规形式粒子加工方法注射成型物理性能额定值单位制测试方法密度1.37g/cm³ISO 1183机械性能额定值单位制测试方法拉伸应力ISO 527-2    断裂, -40°C251MPaISO 527-2    断裂, 23°C170MPaISO 527-2    断裂, 80°C97.0MPaISO 527-2    断裂, 121°C77.0MPaISO 527-2拉伸应变 (断裂, 23°C)3.3%ISO 527-2弯曲模量 (23°C)8400MPaISO 178冲击性能额定值单位制测试方法简支梁缺口冲击强度 (23°C)23kJ/m²ISO 179悬壁梁缺口冲击强度ISO 180    -40°C18kJ/m²ISO 180    23°C26kJ/m²ISO 180热性能额定值单位制测试方法热变形温度 (1.8 MPa, 未退火)203°CISO 75-2/A溶融温度（DSC）220°CISO 3146注射额定值单位制干燥温度80.0°C干燥时间2.0 到 4.0hr建议的最大水分含量0.080%料筒后部温度245 到 275°C料筒中部温度260 到 285°C料筒前部温度270 到 295°C射嘴温度270 到 295°C加工（熔体）温度270 到 295°C模具温度80.0 到 95.0°C注塑压力3.50 到 12.5MPa注射速度快速加纤34% PA6 德国巴斯夫 TG7S 冲击改性 热稳定 草坪 园林设备 坐椅 加纤34% PA6 德国巴斯夫 TG7S 冲击改性 热稳定 草坪 园林设备 坐椅 加纤34% PA6 德国巴斯夫 TG7S 冲击改性 热稳定 草坪 园林设备 坐椅