高抗冲 Ultramid® PA66 德国巴斯夫 C3U 阻燃 电气元件 电子绝缘

高抗冲 Ultramid® PA66 德国巴斯夫 C3U 阻燃 电气元件 电子绝缘 Ultramid® C3UPolyamide 66/6 CopolymerBASF Corporation产品说明：Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness.ApplicationsIt is used for impact resistant electrical insulating parts such as contact bases and plug connector strips.物性信息：基本信息黄卡编号E36632-531680E41871-233722E333174-100976889E333174-101180750特性抗撞击性，良好通用阻燃性用途电气元件电子绝缘通用机构评级EC 1907/2006 (REACH)RoHS 合规性RoHS 合规形式粒子加工方法注射成型多点数据Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)物理性能干燥调节后的单位制测试方法比重1.16--g/cm³ASTM D792, ISO 1183溶化体积流率（MVR） (275°C/5.0 kg)140--cm³/10minISO 1133收缩率 - 流动 (3.18 mm)0.80--%吸水率     饱和8.5--%ASTM D570     饱和, 23°C8.5--%ISO 62     平衡, 50% RH2.9--%ASTM D570     平衡, 23°C, 50% RH2.9--%ISO 62硬度干燥调节后的单位制测试方法球压硬度100--MPaISO 2039-1机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)35001500MPaISO 527-2抗张强度     屈服, 23°C83.0--MPaASTM D638     屈服, 23°C75.045.0MPaISO 527-2伸长率     屈服, 23°C5.0--%ASTM D638     屈服, 23°C4.018%ISO 527-2     断裂, 23°C50--%ASTM D638标称拉伸断裂应变 (23°C)6.0> 50%ISO 527-2弯曲模量 (23°C)3000--MPaASTM D790, ISO 178冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度ISO 179     -30°C4.0--kJ/m²ISO 179     23°C9.035kJ/m²ISO 179简支梁无缺口冲击强度 (23°C)80 kJ/m²无断裂ISO 179悬壁梁缺口冲击强度     -40°C32--J/mASTM D256     23°C43--J/mASTM D256     23°C4.5--kJ/m²ISO 180热性能干燥调节后的单位制测试方法载荷下热变形温度     0.45 MPa, 未退火224--°CASTM D648     1.8 MPa, 未退火91.0--°CASTM D648     1.8 MPa, 未退火70.0--°CISO 75-2/A熔融峰值温度243--°CASTM D3418, ISO 3146高抗冲 Ultramid® PA66 德国巴斯夫 C3U 阻燃 电气元件 电子绝缘 德国巴斯夫pa66, C3U,高抗冲PA66 ,阻燃级pa66,PA66塑胶原料