| 吸湿率 (湿) | 1.1 | % |
| 阻燃性 (干) | HB | UL 94 | |
| 比重 (干) | 1.58 | ASTM D-792 | |
| 成型收缩率 (干) | 0.2/0.5 | % | 旭化成方法 |
| 拉伸强度 (干(湿)) | 235(196) | MPa | ASTM D-638 |
| 抗挠强度 (干(湿)) | 373(304) | MPa | ASTM D-790 |
| 洛氏硬度 | ASTM D-785 | ||
| (干(湿)) | 90(-) | M scale | |
| (干(湿)) | 120(-) | R scale | |
| 抗挠系数 (干(湿)) | 15.5(12.1) | GPa | ASTM D-790 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 127(133) | J/M | ASTM D-256 |
| 断裂延伸率 (干(湿)) | 2.5(3) | % | ASTM D-638 |
| 热变形温度 (1.82MPa,干) | 225 | ℃ | ASTM D-648 |
| 线性膨胀系数 (干) | 2 | ×10-5/K | ASTM D-696 |