技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.15 | % | |
| 熔融指数 | ASTM D-1238 | 2.5 | g/10min | ||
| 物理性能 | 比重 | ASTM D-792 | 1.2 | ||
| 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10 | |
| 机械性能 | 拉伸强度 | 屈服点 | ASTM D-638 | 62 | MPa |
| 断裂点 | ASTM D-638 | 65 | MPa | ||
| 缺口冲击强度 | 23°C | ASTM D-256 | 747 | J/M | |
| 弯曲模量 | ASTM D-790 | 2343 | MPa | ||
| 弯曲强度 | ASTM D-790 | 93 | MPa | ||
| 拉伸率 | 断裂点 | ASTM D-638 | 110 | % | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 157 | °C | |
| 热变形温度 | 1.8MPa | ASTM D-648 | 132 | °C | |
| 线膨胀系数 | ASTM E-831 | 6.8×10 | 1/°C | ||
| 热变形温度 | 0.45MPa | ASTM D-648 | 137 | °C | |