| 吸湿率 (湿) | 1.5 | % |
| 磨耗率 (湿) | 22 | ×10-6kg/1000times | ASTM D-1044 |
| 比重 (干) | 1.52 | ASTM D-792 | |
| 成型收缩率 (干) | 1.0-1.1 | % | 旭化成方法 |
| 断裂延伸率 (干(湿)) | 6(7) | % | ASTM D-638 |
| 抗挠系数 (干(湿)) | 5.6(3.3) | GPa | ASTM D-790 |
| 洛氏硬度 (干(湿)) | 120(108) | R scale | ASTM D-785 |
| 抗挠强度 (干(湿)) | 157(98) | MPa | ASTM D-790 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 34(39) | J/M | ASTM D-256 |
| 洛氏硬度 (干(湿)) | 85(60) | M scale | ASTM D-785 |
| 拉伸强度 (干(湿)) | 98(67) | MPa | ASTM D-638 |
| 线性膨胀系数 (干) | 6 | ×10-5/K | ASTM D-696 |
| 热变形温度 (0.46MPa,干) | 240 | ℃ | ASTM D-648 |
| 阻燃性 (干) | HB | UL 94 | |
| 热变形温度 (1.82MPa,干) | 160 | ℃ | ASTM D-648 |