| 熔体流动速率 | 26 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm3 | ASTM D-792 |
| 屈服拉伸强度 | 25 | MPa | ASTM D-638 |
| 断裂伸长率 | >100 | % | ASTM D-638 |
| 弯曲模量 | 1270 | MPa | ASTM D-790 |
| IZOD缺口冲击强度 | ASTM D-256 | ||
| (23℃) | 88 | J/m | |
| (-10℃) | 44 | J/m |
| 热变形温度 (4.6kgf/cm2) | 103 | ℃ |
| 熔体流动速率 | 26 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm3 | ASTM D-792 |
| 屈服拉伸强度 | 25 | MPa | ASTM D-638 |
| 断裂伸长率 | >100 | % | ASTM D-638 |
| 弯曲模量 | 1270 | MPa | ASTM D-790 |
| IZOD缺口冲击强度 | ASTM D-256 | ||
| (23℃) | 88 | J/m | |
| (-10℃) | 44 | J/m |
| 热变形温度 (4.6kgf/cm2) | 103 | ℃ |