| 吸湿率 (湿) | 1.5 | % |
| 成型收缩率 (干) | 0.5-1.3 | % | 旭化成方法 |
| 磨耗率 (湿) | 8 | ×10-6kg/1000times | ASTM D-1044 |
| 比重 (干) | 1.48 | ASTM D-792 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 34(39) | J/M | ASTM D-256 |
| 洛氏硬度 (干(湿)) | 85(-) | M scale | ASTM D-785 |
| 抗挠系数 (干(湿)) | 5.9(2.9) | GPa | ASTM D-790 |
| 拉伸强度 (干(湿)) | 88(64) | MPa | ASTM D-638 |
| 抗挠强度 (干(湿)) | 147(93) | MPa | ASTM D-790 |
| 断裂延伸率 (干(湿)) | 3(3.5) | % | ASTM D-638 |
| 线性膨胀系数 (干) | 4 | ×10-5/K | ASTM D-696 |
| 热变形温度 (1.82MPa,干) | 191(250) | ℃ | ASTM D-648 |