| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 刚性指数 | 18000 | kg/cm | ASTM D-790 |
| 熔体流动速率 (230℃.2.16kg) | 60 | g/10min | ASTM D-1238L |
| 冲击强度 | 2.3 | kg.cm/cm | ASTM D-256 |
| 洛氏硬度 | 105 | R标尺 | ASTM D-785 |
| 降伏点压力强度 | 370 | kg/cm | ASTM D-638 |
| 降伏点延长 | 10 | % | ASTM D-638 |
| 热变形温度 | 125 | ℃ | ASTM D-648 |
| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 刚性指数 | 18000 | kg/cm | ASTM D-790 |
| 熔体流动速率 (230℃.2.16kg) | 60 | g/10min | ASTM D-1238L |
| 冲击强度 | 2.3 | kg.cm/cm | ASTM D-256 |
| 洛氏硬度 | 105 | R标尺 | ASTM D-785 |
| 降伏点压力强度 | 370 | kg/cm | ASTM D-638 |
| 降伏点延长 | 10 | % | ASTM D-638 |
| 热变形温度 | 125 | ℃ | ASTM D-648 |