TPE美国杜邦4069 高性能级
TPE美国杜邦4069的详细描述：
DuPont Performance Polymers Hytrel® 4069 TPC-ET (Unverified Data**) 物性表
物理性能额定值 (公制)额定值 (英制)测试方法比重1.11 g/cc1.11 g/ccASTM D792密度1.11 g/cc0.0401 lb/in³ISO 1183Water Absorption0.20 %@Temperature 23.0 °C
0.20 %@Temperature 73.4 °F
Equilibrium 50%RH; ISO 620.70 %
@Temperature 23.0 °C
0.70 %@Temperature 73.4 °F
Immersion 24h; ASTM D5700.70 %
@Temperature 23.0 °C
Immersion 24h; ISO 620.70 %
@Temperature 23.0 °C
Saturation, immersed; ISO 62线性成型收缩率0.0080 cm/cm0.0080 in/inFlow; ASTM D955线性成型收缩率,Flow0.0080 cm/cm@Thickness 2.00 mm
0.0080 in/in@Thickness 0.0787 in
ISO 294-4线性成型收缩率，横向0.0080 cm/cm@Thickness 2.00 mm
ISO 294-4熔体流动速率8.5 g/10 min@Load 2.16 kg, Temperature 220 °C
8.5 g/10 min@Load 4.76 lb, Temperature 428 °F
ASTM D12388.5 g/10 min
@Load 2.16 kg, Temperature 220 °C
ISO 1133化合物熔体指数7.7 g/10 min@Load 2.16 kg, Temperature 220 °C
7.7 g/10 min@Load 4.76 lb, Temperature 428 °F
cm3/10 min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法肖氏硬度 (邵氏 D)<= 37<= 37ISO 868<= 40<= 40ASTM D2240
33
@Time 15.0 sec
33@Time 0.00417 hour
ISO 868抗张强度(断裂)20.0 MPa@Temperature 23.0 °C
2900 psi@Temperature 73.4 °F
ASTM D63828.0 MPa
@Temperature 23.0 °C
4060 psi@Temperature 73.4 °F
ISO 527 (1BA bar)抗张强度2.40 MPa@Strain 5.00 %, Temperature 23.0 °C
348 psi@Strain 5.00 %, Temperature 73.4 °F
ASTM D6383.20 MPa
@Strain 10.0 %, Temperature 23.0 °C
464 psi@Strain 10.0 %, Temperature 73.4 °F
ISO 527 (1BA bar)3.50 MPa
@Strain 10.0 %, Temperature 23.0 °C
508 psi@Strain 10.0 %, Temperature 73.4 °F
ASTM D6386.70 MPa
@Strain 50.0 %, Temperature 23.0 °C
972 psi@Strain 50.0 %, Temperature 73.4 °F
ISO 527 (1BA bar)伸长率 (断裂)>= 50 %@Temperature 23.0 °C
>= 50 %@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)>= 300 %
@Temperature 23.0 °C
>= 300 %@Temperature 73.4 °F
ISO 527 (1BA bar)650 %
@Temperature 23.0 °C
650 %@Temperature 73.4 °F
ISO 527 (1BA bar)700 %
@Temperature 23.0 °C
700 %@Temperature 73.4 °F
ASTM D638800 %
@Temperature 23.0 °C
800 %@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)拉伸模量0.0450 GPa@Temperature 23.0 °C
6.53 ksi@Temperature 73.4 °F
ISO 527弯曲模量0.0280 GPa@Temperature 100 °C
4.06 ksi@Temperature 212 °F
ASTM D7900.0280 GPa
@Temperature 100 °C
ISO 1780.0470 GPa
@Temperature 23.0 °C
6.82 ksi@Temperature 73.4 °F
ISO 1780.0550 GPa
@Temperature 23.0 °C
7.98 ksi@Temperature 73.4 °F
ASTM D7900.172 GPa
@Temperature -40.0 °C
24.9 ksi@Temperature -40.0 °F
ISO 178悬壁梁缺口冲击强度NB@Temperature -40.0 °C
NB@Temperature -40.0 °F
ASTM D256NB
@Temperature 23.0 °C
NB@Temperature 73.4 °F
ASTM D256NB
@Temperature -40.0 °C
ISO 180/1ANB
@Temperature 23.0 °C
ISO 180/1A简支梁无缺口冲击强度NB@Temperature -30.0 °C
NB@Temperature -22.0 °F
ISO 179/1eUNB
@Temperature 23.0 °C
ISO 179/1eU简支梁缺口冲击强度NB@Temperature -40.0 °C
ISO 179/1eANB
@Temperature -30.0 °C
ISO 179/1eANB
@Temperature 23.0 °C
ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率4.00e+12 ohm-cm@Temperature 23.0 °C
4.00e+12 ohm-cm@Temperature 73.4 °F
IEC 60093表面电阻3.00e+14 ohm@Temperature 23.0 °C
3.00e+14 ohm@Temperature 73.4 °F
IEC 60093介电常数4.7@Frequency 1.00e+6 Hz, Temperature 23.0 °C
4.7@Frequency 1.00e+6 Hz, Temperature 73.4 °F
IEC 602504.8
@Frequency 100 Hz, Temperature 23.0 °C
4.8@Frequency 100 Hz, Temperature 73.4 °F
IEC 60250介电强度18.0 kV/mm@Temperature 23.0 °C
457 kV/in@Temperature 73.4 °F
IEC 60243-1耗散因数0.013@Frequency 100 Hz, Temperature 23.0 °C
0.013@Frequency 100 Hz, Temperature 73.4 °F
IEC 602500.020
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
0.020@Frequency 1.00e+6 Hz, Temperature 73.4 °F
IEC 60250相比耐漏电起痕指数(CTI)>= 600 V@Temperature 23.0 °C
>= 600 V@Temperature 73.4 °F
IEC 60112>= 600 V
@Thickness 3.00 mm, Temperature 23.0 °C
>= 600 V@Thickness 0.118 in, Temperature 73.4 °F
UL 746A热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动500 µm/m-°C@Temperature -40.0 - 23.0 °C
278 µin/in-°F@Temperature -40.0 - 73.4 °F
ASTM E 831500 µm/m-°C
@Temperature 23.0 - 55.0 °C
278 µin/in-°F@Temperature 73.4 - 131 °F
ASTM E 831500 µm/m-°C
@Temperature 55.0 - 120 °C
278 µin/in-°F@Temperature 131 - 248 °F
ASTM E 831500 µm/m-°C
@Temperature -40.0 - 23.0 °C
ISO 11359-1/-2500 µm/m-°C
@Temperature 23.0 - 55.0 °C
ISO 11359-1/-2500 µm/m-°C
@Temperature 55.0 - 120 °C
ISO 11359-1/-2线性热膨胀系数,横向流动190 µm/m-°C@Temperature 23.0 - 55.0 °C
106 µin/in-°F@Temperature 73.4 - 131 °F
ISO 11359-1/-2190 µm/m-°C
@Temperature 55.0 - 120 °C
106 µin/in-°F@Temperature 131 - 248 °F
ISO 11359-1/-2192 µm/m-°C
@Temperature 55.0 - 120 °C
107 µin/in-°F@Temperature 131 - 248 °F
ASTM E 831219 µm/m-°C
@Temperature 23.0 - 55.0 °C
122 µin/in-°F@Temperature 73.4 - 131 °F
ASTM E 831270 µm/m-°C
@Temperature -40.0 - 23.0 °C
150 µin/in-°F@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2277 µm/m-°C
@Temperature -40.0 - 23.0 °C
154 µin/in-°F@Temperature -40.0 - 73.4 °F
ASTM E 831熔融温度193 °C379 °F10°C/min; ISO 11357-1/-3193 °C379 °FASTM D3418载荷下热变形温度(0.46 MPa)50.0 °C122 °FISO 75-1/-2
55.0 °C131 °FASTM D648脆化温度-95.0 °C-139 °FISO 974玻璃化转变温度，Tg-50.0 °C-58.0 °F10°C/min; ISO 11357-1/-2UL RTI50.0 °C
@Thickness 1.50 mm
122 °F@Thickness 0.0591 in
UL 746B50.0 °C
@Thickness 3.00 mm
122 °F@Thickness 0.118 in
UL 746B分类
聚合物是由许多较小而结构简单的小分子(monomer)，藉共价键来组合而成的。 TPE(01)本色( 30度-120度 ),(02)透明( 30度-120度 ),(03)黑色( 30度-120度 ) ,(04)TPE射粘级 4.TPE 不锈纲级 ,(05)TPE食品级 ,(06)TPE挤出级, (07)TPE片材级 ,(08)TPE阻燃 ,(09)TPE耐磨级, (10)TPE烯烃级 ,(11)TPE阻隔级, (12)TPE导电级 ,(13)TPE改性, (14)TPE吹塑级 ,(15)发泡级,(16)薄膜级,(17)软胶级