| 密度 | 0.9 | G/cm | ISO 1183 |
| 熔体流动速率 (230°C/2.16 kg) | 8 | g/10min | ISO 1133 |
| 拉伸模量 | 1100 | Mpa | ISO 527-2/1 |
| 抗张强度 (Yield) | 22 | Mpa | ISO 527-2/50 |
| 抗张伸展率 (Yield) | 6 | % | ISO 527-2/50 |
| Lzod缺口冲击强度 (23℃) | 15 | ISO 180/1A | |
| 硬度 (Shore D) | 58 | ISO 868 |
| 维卡软化温度 | 145 | ℃ | ISO 306/A50 |