LEXAN PC 925A-116阻燃PC---Lexan* 925A Polycarbonate (PC) resin is a non-filled, injection moldable grade of non-chlorinated, non-brominated flame retardant systems that has an UL-94 V0 rating. Lexan 925A is available in transparent and tinted color options and is a general-purpose resin ideal for a wide variety of applications
LEXAN PC 925A-116产品说明：
Lexan*925A聚碳酸酯（PC）树脂是一种非填充、可注射成型的非氯化、非溴阻燃系统，具有UL-94 V0等级。Lexan 925A有透明和着色两种颜色可供选择，是广泛应用的理想通用树脂。
LEXAN PC 925A-116
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 13 g/10 min @Load 1.20 kg, Temperature 300 °C | 13 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 67.0 MPa | 9720 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 125 % | 125 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D638 |
| 弯曲强度 | 101 MPa | 14600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| 落锤总能量 | 79.0 J @Temperature 23.0 °C | 58.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 250 - 400 V | 250 - 400 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 80.0 - 150 mm/min | 3.16 - 5.91 in/min | UL 746A |