20% PTFE增强POM美国杜邦100AF

20% PTFE铁氟龙增强POM美国杜邦100AF物性表ACETAL RESIN20% PTFE 纤维DuPont Performance Polymers产品说明：20% Teflon® Fiber Filled High Viscosity Acetal Homopolymer with Low Wear and Low Friction性能项目试验条件[状态]测试方法测试数据数据单位基本性能密度ASTM D-7921.54物理性能扩散因数+73℉(+23℃)106HzASTM D-1500.009绝缘系数+73℉(+23℃)10²to106HzASTM D-1503.1电阻系数+73℉(+23℃)0.2%H2OASTM D-2573×1016ohm-cm机械性能伸张强度+23℃ASTM D-63852.4MPa压缩应力+23℃@1%Def.ASTM D-69531.0MPa拉力冲击抵抗力+73℉D1822Long50ft.lb/in2绝缘强度Short Time,90 milsASTM D-149400(125mils)V/mil压缩应力+73°F@1%Def.ASTM D-6954.5MPsi压缩应力+73°F@10%Def.ASTM D-69513.0MPsi弯曲疲劳忍耐限度+23℃ASTM D-67124.8MPa挠曲系数+158℉在25℃下190MPsi挠曲系数+73℉在25℃下340MPsi伸张强度+212℉ASTM D-6384.0MPsi弯曲降服强+23℃ASTM D-79072.4MPaIzod冲击强度40℃ASTM D-25653.4j/m弹性系数+73℉ASTM D-638420MPsi断裂时之拉力伸张度+212℉(+100℃)ASTM D-638250%伸张强度+100℃ASTM D-63828.3MPa断裂时之拉力伸张度+73℉(+23℃)ASTM D-63822%拉力冲击抵抗力+23℃D1822Long102kj/m2热变形温度66psiASTM D-648334℉挠曲系数+250℉在25℃下80MPsi挠曲系数+70℃在25℃下1310MPa电弧抵抗力120mil(3.1mm)ASTM D-495183no trackingSec.洛氏硬度ASTM D-785M78,R118剪力+73℉ASTM D-7328.0MPsi弯曲疲劳忍耐限度+73℉ASTM D-6713.6MPsi剪力+23℃ASTM D-73255.2MPa挠曲系数-68℉在25℃下520MPsi绝缘强度Short Time,2.3mmASTM D-14915.8(3.2mm)MV/m伸张强度+250℉ASTM D-6383.1MPsi断裂时之拉力伸张度-68℉(-55℃)ASTM D-63815%伸张强度+158℉ASTM D-6385.3MPsi负载下之变形2000psi@+122℉(14Mpa@50℃)ASTM D-6210.6%挠曲系数+23℃在25℃下2340MPa挠曲系数+122℃在25℃下550MPa弯曲降服强+73℉ASTM D-79010.5MPsi伸张强度+122℃ASTM D-63820.7MPaIzod冲击强度+73℉ASTM D-2561.2ft.lb/in摩擦系数+73℉(+23℃)动态ThrustWasherTest30.14挠曲系数+212℉在25℃下110MPsi断裂时之拉力伸张度+158℉(+70℃)ASTM D-63850%挠曲系数+100℃在25℃下700MPa伸张强度+73℉ASTM D-6387.6MPsiIzod冲击强度-40℉ASTM D-2561.0ft.lb/in伸张强度+70℃ASTM D-63836.5MPa伸张强度-68℉ASTM D-63810.9MPsi弹性系数+23℃ASTM D-6382895MPa挠曲系数-55℃在25℃下3585MPa压缩应力+23℃@10%Def.ASTM D-69589.6MPa断裂时之拉力伸张度+250℉(+122℃)ASTM D-638>260%Izod冲击强度+23℃ASTM D-25664.1j/m伸张强度-55℃ASTM D-63875MPa加工性能吸水量浸泡均衡点+73℉(+23℃)ASTM D-5700.72%吸水量Equil.50%R.h.+73℉(+23℃)ASTM D-5700.18%吸水量24hrs浸泡+73℉(+23℃)ASTM D-5700.20%热性能热变形温度0.5MPaASTM D-648168℃热变形温度1.8MPaASTM D-648118℃线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃线性热膨胀系数-40 to +85℉ASTM D-6965.810-5in/in℉线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃熔点ASTM D-2133347℉可燃烧性UL-9494HB热变形温度264psiASTM D-648244°F线性热膨胀系数+85 to +140℉ASTM D-6966.810-5in/in℉熔点ASTM D-2133175℃