物理性能测试条件测试方法测试结果单位密度 / 比重ASTMD7921.39g/cm³
ISO11831.39g/cm³干ASTM D-7921.39
磨耗率湿ASTM D-104415×10-6kg/1000times收缩率干旭化成方法0.4/0.9%TD内部方法0.90%MD内部方法0.40%机械性能测试条件测试方法测试结果单位断裂延伸率干(湿)ASTM D-6383(5)%抗挠强度干(湿)ASTM D-790289(216)Mpa抗挠系数干(湿)ASTM D-7909.3(6.3)GPa抗张强度
ASTMD638186Mpa拉伸模量23°CISO527-210000Mpa拉伸强度干(湿)ASTM D-638186(132)Mpa拉伸应变断裂,23°CISO527-23.0%拉伸应力断裂,23°CISO527-2190Mpa洛氏硬度干(湿)ASTM D-78596(75)M Scale干(湿)ASTM D-785120(112)R scale
ASTM D785M96
伸长率断裂ASTMD6383.0%弯曲模量
ASTMD7909300Mpa23°CISO1789000Mpa
ASTM D790/ISO 1789320(MPa)kg·cm/cm(J/M)ft·lb/in弯曲强度
ASTM D790/ISO 178289(MPa)kg·cm/cm(J/M)ft·lb/in
ASTMD790289Mpa弯曲应力23°CISO178275Mpa悬臂梁式缺口冲击强度干(湿)ASTM D-256127(147)J/m热性能测试条件测试方法测试结果单位比热
1590J/kg/°C比热容干
1590J/(kg.k)导热率干
0.3W/(m.K)导热系数
0.30W/m/K燃烧性(率)
UL94HB
热变形温度
ASTM D648/ISO 75250℃(℉)0.45MPa,未退火ASTMD648260°C0.45MPa,未退火ISO75-2/B265°C1.8MPa,未退火ASTMD648250°C1.8MPa,未退火ISO75-2/A250°C1.82MPa,干ASTM D-648250℃0.46MPa,干ASTM D-648260℃线形热膨胀系数MDASTMD6963E-05cm/cm/°C线性膨胀系数
ASTM D696/ISO 113593mm/mm.℃干ASTM D-6963×10-5/K阻燃性干UL 94HB
电气性能测试条件测试方法测试结果单位表面电阻率
ASTMD2571E+15ohms
IEC600931E+15ohms介电强度
ASTMD14928KV/mm
IEC60243-128KV/mm漏电起痕指数3.00mmIEC60112600V耐电弧性
ASTM D495/IEC 60112124
体积电阻率
ASTMD2571E+15ohms·cm23°CIEC600931E+15ohms·cm冲击性能测试条件测试方法测试结果单位简支梁缺口冲击强度
ISO17911kJ/m²简支梁无缺口冲击强度
ISO17972kJ/m²悬壁梁缺口冲击强度
ASTMD256130J/m可燃性(Flammability)测试条件测试方法测试结果单位FlameRating0.75mmUL94HB
极限氧指数
ASTMD286323%硬度Hardness测试条件测试方法测试结果单位洛氏硬度M计秤ASTMD78596
R计秤ASTMD785120
M计秤ISO2039-296
R计秤ISO2039-2120
物性性能测试条件测试方法测试结果单位比重(密度)
ASTM D792/ISO 11831.39
成型收缩率
ASTM D9550.4-0.9%吸水率 23℃/24H
ASTM D570/ISO 621.7%基本性能测试条件测试方法测试结果单位吸湿率湿
1.7%其他性能测试条件测试方法测试结果单位氧指数干ASTM D-286323%
PA性质:结晶性热可塑性塑料,有明显熔点,Nylon6 Tm为220~230℃,Nylon66则为260~270℃,Nylon本身具吸水基故有吸水性,成形前须干燥,温度过高干燥则尼龙粒变色。
优点:1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性、耐磨性佳、耐药品性优;4、低温特性佳;5、具自熄性
用途:电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类:防静电PA,导电PA,加纤防火PA,防火PA,抗紫外线耐候PA,高温挤出级PA。