Hostaform® LX90Z XAP² ™
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Preliminary Data Sheet
Hostaform® acetal copolymer grade LX90Z XAP2 ™ is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform® LX90Z XAP2 ™ has lower volatile emissions as required for some automotive interiors.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
Low Emission Performance [VDA-275] <5 PPM
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.43 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.4 | % | ISO 294-4 |
| 流动方向 | 2.3 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 0.75 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2700 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 54.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 8.0 | % | ISO 527-2/1A/50 |
| 弯曲模量 (23°C) | 2900 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 | |||
| 0.45 MPa, 未退火 | 147 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 90.0 | °C | ISO 75-2/A |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.0E-4 | cm/cm/°C | ISO 11359-2 |