FL 00209乙烯-醋酸乙烯共聚物#|EVA
埃克森美孚
物性信息：
| 熔流率 | 2.1 | g/10 min | ASTM D1238 |
| 醋酸乙烯含量 (190°C/2.16 kg)) | 9.4 | wt% | ExxonMobil Method |
| 支撐硬度 (支撐 A, 15 秒) | 93 | ISO 868 |
| 拉伸模量 | 90.0 | MPa | ISO 527-2 |
| 割线模量 (1% 正割, MD) | 90.0 | MPa | ASTM D882 |
| (1% 正割, TD) | 95.0 | MPa | ASTM D882 |
| 抗张强度 (MD: 断裂) | 28.0 | MPa | ASTM D882 |
| (TD: 断裂) | 27.0 | MPa | ASTM D882 |
| 伸长率 (MD: 断裂) | 550 | % | ASTM D882 |
| (TD: 断裂) | 650 | % | ASTM D882 |
| 落锤冲击 | 390 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 (MD) | 120 | g | ASTM D1922 |
| (TD) | 190 | g | ASTM D1922 |
| 维卡软化温度 | 78.5 | °C | ASTM D1525 |