BASF Ultrason E 2010 G6 30% Glass Filled PES 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.60 g/cc0.0578 lb/in³ISO 1183吸水率1.6 %1.6 %ISO 62平衡吸湿0.60 %0.60 %23°C/50% R.H.; ISO 62粘度测试56 cm³/g56 cm³/gViscosity number线性成型收缩率,Flow0.0028 cm/cm0.0028 in/inISO 294线性成型收缩率，横向0.0058 cm/cm0.0058 in/inISO 294熔体流动速率25 g/10 min

@Load 10.0 kg, Temperature 360 °C

25 g/10 min

@Load 22.0 lb, Temperature 680 °F

ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法球压硬度224 MPa32500 psiISO 2039-1抗张强度(断裂)140 MPa20300 psi5mm/min; ISO 527-2
100 MPa

@Temperature 140 °C

14500 psi

@Temperature 284 °F

125 MPa

@Temperature 100 °C

18100 psi

@Temperature 212 °F

135 MPa

@Temperature 60.0 °C

19600 psi

@Temperature 140 °F

150 MPa

@Temperature 20.0 °C

21800 psi

@Temperature 68.0 °F

抗张强度31.0 MPa

@# of Cycles 1.00e+7 , Temperature 180 °C

4500 psi

@# of Cycles 1.00e+7 , Temperature 356 °F

38.0 MPa

@# of Cycles 1.00e+6 , Temperature 180 °C

5510 psi

@# of Cycles 1.00e+6 , Temperature 356 °F

43.0 MPa

@# of Cycles 100000 , Temperature 180 °C

6240 psi

@# of Cycles 100000 , Temperature 356 °F

50.0 MPa

@Strain 0.600 %, Temperature 160 °C

7250 psi

@Strain 0.600 %, Temperature 320 °F

ISO 527
50.0 MPa

@Strain 0.500 %, Temperature 23.0 °C

7250 psi

@Strain 0.500 %, Temperature 73.4 °F

ISO 527
75.0 MPa

@Strain 1.00 %, Temperature 160 °C

10900 psi

@Strain 1.00 %, Temperature 320 °F

ISO 527
80.0 MPa

@Strain 1.40 %, Temperature 160 °C

11600 psi

@Strain 1.40 %, Temperature 320 °F

ISO 527
80.0 MPa

@Strain 1.00 %, Temperature 23.0 °C

11600 psi

@Strain 1.00 %, Temperature 73.4 °F

ISO 527
125 MPa

@Strain 1.50 %, Temperature 23.0 °C

18100 psi

@Strain 1.50 %, Temperature 73.4 °F

ISO 527抗张强度(屈服)140 MPa20300 psi50mm/min; ISO 527-2伸长率 (断裂)1.9 %1.9 %5mm/min; ISO 527-2屈服伸长率1.9 %1.9 %50mm/min; ISO 527-2
0.189 %

@Time 3600 sec, Pressure 15.0 MPa

0.189 %

@Time 1.00 hour, Pressure 2180 psi

ISO 899
0.19 %

@Pressure 15.0 MPa, Time 360000 sec

0.19 %

@Pressure 2180 psi, Time 100 hour

ISO 899
0.20 %

@Pressure 15.0 MPa, Time 3.60e+7 sec

0.20 %

@Pressure 2180 psi, Time 10000 hour

ISO 899
0.20 %

@Pressure 10.0 MPa, Time 360000 sec

0.20 %

@Pressure 1450 psi, Time 100 hour

180°C; ISO 899
0.20 %

@Time 3600 sec, Pressure 10.0 MPa

0.20 %

@Time 1.00 hour, Pressure 1450 psi

180°C; ISO 899
0.25 %

@Pressure 10.0 MPa, Time 3.60e+7 sec

0.25 %

@Pressure 1450 psi, Time 10000 hour

180°C; ISO 899
0.30 %

@Time 3600 sec, Pressure 20.0 MPa

0.30 %

@Time 1.00 hour, Pressure 2900 psi

180°C; ISO 899
0.30 %

@Pressure 20.0 MPa, Time 360000 sec

0.30 %

@Pressure 2900 psi, Time 100 hour

180°C; ISO 899
0.30 %

@Time 3600 sec, Pressure 30.0 MPa

0.30 %

@Time 1.00 hour, Pressure 4350 psi

180°C; ISO 899
0.35 %

@Time 3600 sec, Pressure 30.0 MPa

0.35 %

@Time 1.00 hour, Pressure 4350 psi

180°C; ISO 899
0.38 %

@Pressure 30.0 MPa, Time 360000 sec

0.38 %

@Pressure 4350 psi, Time 100 hour

180°C; ISO 899
0.40 %

@Pressure 30.0 MPa, Time 3.60e+7 sec

0.40 %

@Pressure 4350 psi, Time 10000 hour

ISO 899
0.40 %

@Time 3600 sec, Pressure 40.0 MPa

0.40 %

@Time 1.00 hour, Pressure 5800 psi

180°C; ISO 899
0.40 %

@Pressure 20.0 MPa, Time 3.60e+7 sec

0.40 %

@Pressure 2900 psi, Time 10000 hour

180°C; ISO 899
0.40 %

@Pressure 30.0 MPa, Time 360000 sec

0.40 %

@Pressure 4350 psi, Time 100 hour

ISO 899
0.50 %

@Pressure 40.0 MPa, Time 360000 sec

0.50 %

@Pressure 5800 psi, Time 100 hour

ISO 899
0.50 %

@Time 3600 sec, Pressure 50.0 MPa

0.50 %

@Time 1.00 hour, Pressure 7250 psi

180°C; ISO 899
0.55 %

@Time 3600 sec, Pressure 45.0 MPa

0.55 %

@Time 1.00 hour, Pressure 6530 psi

ISO 899
0.60 %

@Pressure 45.0 MPa, Time 360000 sec

0.60 %

@Pressure 6530 psi, Time 100 hour

ISO 899
0.78 %

@Time 3600 sec, Pressure 60.0 MPa

0.78 %

@Time 1.00 hour, Pressure 8700 psi

ISO 899
0.80 %

@Pressure 60.0 MPa, Time 360000 sec

0.80 %

@Pressure 8700 psi, Time 100 hour

ISO 899
0.80 %

@Pressure 50.0 MPa, Time 360000 sec

0.80 %

@Pressure 7250 psi, Time 100 hour

180°C; ISO 899
0.90 %

@Pressure 30.0 MPa, Time 3.60e+7 sec

0.90 %

@Pressure 4350 psi, Time 10000 hour

ISO 899
0.90 %

@Pressure 60.0 MPa, Time 3.60e+7 sec

0.90 %

@Pressure 8700 psi, Time 10000 hour

ISO 899
0.99 %

@Time 3600 sec, Pressure 75.0 MPa

0.99 %

@Time 1.00 hour, Pressure 10900 psi

ISO 899
1.1 %

@Pressure 75.0 MPa, Time 360000 sec

1.1 %

@Pressure 10900 psi, Time 100 hour

ISO 899
1.23 %

@Pressure 75.0 MPa, Time 3.60e+7 sec

1.23 %

@Pressure 10900 psi, Time 10000 hour

ISO 899
1.5 %

@Pressure 40.0 MPa, Time 3.60e+7 sec

1.5 %

@Pressure 5800 psi, Time 10000 hour

180°C; ISO 899
2.5 %

@Pressure 50.0 MPa, Time 3.60e+7 sec

2.5 %

@Pressure 7250 psi, Time 10000 hour

180°C; ISO 899
6.1 %

@Pressure 45.0 MPa, Time 3.60e+7 sec

6.1 %

@Pressure 6530 psi, Time 10000 hour

ISO 899Creep Strength22.0 MPa

@Time 3.60e+7 sec

3190 psi

@Time 10000 hour

in water at 95°C
30.0 MPa

@Time 3.60e+6 sec

4350 psi

@Time 1000 hour

in water at 95°C
41.0 MPa

@Time 360000 sec

5950 psi

@Time 100 hour

in water at 95°C
55.0 MPa

@Time 36000 sec

7980 psi

@Time 10.0 hour

in water at 95°C弹性模量9.80 GPa

@Temperature 160 °C

1420 ksi

@Temperature 320 °F

ISO 527
9.85 GPa

@Temperature 60.0 °C

1430 ksi

@Temperature 140 °F

ISO 527
9.90 GPa

@Temperature 20.0 °C

1440 ksi

@Temperature 68.0 °F

ISO 527
10.0 GPa

@Temperature 120 °C

1450 ksi

@Temperature 248 °F

ISO 527拉伸模量10.0 GPa1450 ksiISO 527-2Fatigue Strength43.0 MPa

@# of Cycles 1.00e+7

6240 psi

@# of Cycles 1.00e+7

52.0 MPa

@# of Cycles 1.00e+6

7540 psi

@# of Cycles 1.00e+6

65.0 MPa

@# of Cycles 100000

9430 psi

@# of Cycles 100000

剪切模量0.200 GPa

@Temperature 225 °C

29.0 ksi

@Temperature 437 °F

ISO 6721
0.900 GPa

@Temperature 200 °C

131 ksi

@Temperature 392 °F

ISO 6721
0.950 GPa

@Temperature 100 °C

138 ksi

@Temperature 212 °F

ISO 6721
1.00 GPa

@Temperature 50.0 °C

145 ksi

@Temperature 122 °F

ISO 6721悬壁梁缺口冲击强度8.00 kJ/m²3.81 ft-lb/in²ISO 180/A
8.00 kJ/m²

@Temperature -30.0 °C

3.81 ft-lb/in²

@Temperature -22.0 °F

ISO 180/A悬壁梁无缺口冲击强度42.0 kJ/m²

@Temperature 120 °C

20.0 ft-lb/in²

@Temperature 248 °F

ISO 179/1eU
50.0 kJ/m²

@Temperature 25.0 °C

23.8 ft-lb/in²

@Temperature 77.0 °F

ISO 179/1eU
57.0 kJ/m²

@Temperature -25.0 °C

27.1 ft-lb/in²

@Temperature -13.0 °F

ISO 179/1eU
59.0 kJ/m²

@Temperature 0.000 °C

28.1 ft-lb/in²

@Temperature 32.0 °F

ISO 179/1eU