| 密度 | 1.59 g/cc | 0.0574 lb/in³ | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0040 cm/cm | 0.0040 in/in | DAM; ISO 294-4 2577 |
| 抗张强度(断裂) | 215 MPa | 31200 psi | 50%RH; ISO 527-1/-2 |
| 250 MPa | 36300 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 12.67 MPa @Strain 0.0900 %, Temperature 0.000 °C | 1838 psi @Strain 0.0900 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 13.51 MPa @Strain 0.0900 %, Temperature -20.0 °C | 1959 psi @Strain 0.0900 %, Temperature -4.00 °F | 50%RH; ISO 11403-1 -2 | |
| 14.93 MPa @Strain 0.400 %, Temperature 150 °C | 2165 psi @Strain 0.400 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 15.94 MPa @Strain 0.100 %, Temperature 0.000 °C | 2312 psi @Strain 0.100 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 16.26 MPa @Strain 0.110 %, Temperature 23.0 °C | 2358 psi @Strain 0.110 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 17.84 MPa @Strain 0.120 %, Temperature 40.0 °C | 2587 psi @Strain 0.120 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 17.96 MPa @Strain 0.120 %, Temperature -20.0 °C | 2605 psi @Strain 0.120 %, Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 18.1 MPa @Strain 0.130 %, Temperature 23.0 °C | 2630 psi @Strain 0.130 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 20.09 MPa @Strain 0.360 %, Temperature 90.0 °C | 2914 psi @Strain 0.360 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 21.04 MPa @Strain 0.530 %, Temperature 150 °C | 3052 psi @Strain 0.530 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 25.66 MPa @Strain 0.250 %, Temperature 40.0 °C | 3722 psi @Strain 0.250 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 | |
| 29.88 MPa @Strain 0.400 %, Temperature 90.0 °C | 4334 psi @Strain 0.400 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 32.77 MPa @Strain 1.52 %, Temperature 150 °C | 4753 psi @Strain 1.52 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 40.98 MPa @Strain 2.67 %, Temperature 150 °C | 5944 psi @Strain 2.67 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 45.0 MPa @Strain 2.00 %, Temperature 150 °C | 6530 psi @Strain 2.00 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 46.47 MPa @Strain 3.81 %, Temperature 150 °C | 6740 psi @Strain 3.81 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 49.0 MPa @Strain 1.45 %, Temperature 90.0 °C | 7110 psi @Strain 1.45 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 55.95 MPa @Strain 7.24 %, Temperature 150 °C | 8115 psi @Strain 7.24 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 56.17 MPa @Strain 3.50 %, Temperature 150 °C | 8147 psi @Strain 3.50 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 56.72 MPa @Strain 0.360 %, Temperature 0.000 °C | 8227 psi @Strain 0.360 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 | |
| 58.41 MPa @Strain 9.14 %, Temperature 150 °C | 8472 psi @Strain 9.14 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 |