![均聚PP/韩国大林/HP602N 抗冲击 家用器皿 玩具](http://img.11467.com/2021/06-22/3701787368.jpg)
密度 | 0.9 | g/cm | ASTM D-1505 |
熔体流动速率 (230℃,2.16kg) | 12.5 | g/10min | ASTM D-1238L |
断裂伸长率 | 12 | % | ASTM D-638 |
弯曲模量 | 16000 | kg/cm | ASTM D-790 |
洛氏硬度 | 104 | R scale | ASTM D-785 |
IZOD冲击强度 (23℃) | 3 | kg.cm/cm | ASTM D-256 |
屈服拉伸强度 | 350 | kg/cm | ASTM D-638 |
热变形温度 (0.46N/mm) | 107 | ℃ | ASTM D-648 |