熔体流动速率 | 20 | g/10min | ASTM D-1238 |
屈服拉伸强度 | 400 | kg/cm | ASTM D-638 |
断裂伸长率 | <20 | % | ASTM D-638 |
IZOD缺口冲击强度 (23℃) | 3 | kg.cm/cm | ASTM D-256 |
弯曲模量 | 21000 | kg/cm | ASTM D790 |
洛氏硬度 | 107 | R | ASTM D-785 |
维卡软化点 | 156 | ℃ | ASTM D-1525 |
热变形温度 | 140 | ℃ | ASTM D-648 |
熔体流动速率 | 20 | g/10min | ASTM D-1238 |
屈服拉伸强度 | 400 | kg/cm | ASTM D-638 |
断裂伸长率 | <20 | % | ASTM D-638 |
IZOD缺口冲击强度 (23℃) | 3 | kg.cm/cm | ASTM D-256 |
弯曲模量 | 21000 | kg/cm | ASTM D790 |
洛氏硬度 | 107 | R | ASTM D-785 |
维卡软化点 | 156 | ℃ | ASTM D-1525 |
热变形温度 | 140 | ℃ | ASTM D-648 |