POE/1881G/陶氏杜邦增韧,透明,高强度高抗冲薄膜级医用级吹膜注塑
2023-12-19 06:25 浏览:30次
物理性能额定值单位测试方法
比重 | 0.904 | g/cm³ | ASTM D792 |
熔流率 (190℃/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
机械性能额定值单位测试方法
摩擦系数 (与自身 - 动态) | 0.15 |
| ASTM D1894 |
薄膜额定值单位测试方法
薄膜厚度 (经测试) | 51 | µm |
|
膜刺穿强度 (51 µm) | 8.09 | J | Internal Method |
膜刺穿力 (51 µm) | 82.3 | N | Internal Method |
膜耐刺穿性 (51 µm) | 21.9 | J/cm³ | Internal Method |
割线模量 (2% 正割, MD : 51 µm) | 97.4 | MPa | ASTM D882 |
(2% 正割, TD : 51 µm) | 96.9 | MPa | ASTM D882 |
抗张强度 (MD : 屈服, 51 µm) | 8.07 | MPa | ASTM D882 |
|
|
|
|
(TD : 屈服, 51 µm) | 7.17 | MPa | ASTM D882 |
(MD : 断裂,51 µm) | 45.4 | MPa | ASTM D882 |
(TD : 断裂,51µm) | 42.5 | MPa | ASTM D882 |
伸长率 (MD : 断裂, 51 µm) | 590 | % | ASTM D882 |
(TD : 断裂, 51 µm) | 630 | % | ASTM D882 |
落锤冲击 (51 µm) | > 830 | g | ASTM D1709B |
埃尔曼多夫抗撕强度 (MD : 51 µm) | 560 | g | ASTM D1922 |
(TD : 51 µm) | 730 | g | ASTM D1922 |
始封温度 (51 µm) | 85.0 | ℃ | Internal Method |
阻塞力 | 70 | g | ASTM D3354-89 |
热性能额定值单位测试方法
维卡软化温度 | 86.0 | ℃ | ASTM D1525 |
溶融温度 (DSC) | 100 | ℃ | Internal Method |
光学性能额定值单位测试方法
光泽度 (20°, 50.8 µm) | 112 |
| ASTM D2457 |
透明度 (50.8 µm) | 83.0 |
| ASTM D1746 |
雾度 (50.8 µm) | 3.2 | % | ASTM D1003 |