PC韩国LG 1201-10P 耐热级 食品级 高冲击 高清晰度 一次性餐具材料颗粒
LG Chemical Lupoy 1201-10 Polycarbonate Resin
Polymer,Thermoplastic,Polycarbonate (PC)
LG Chemical
产品说明:
说明： LUPOY PC 1201-10 树脂专为挤出和注塑产品而设计。它表现出耐热性、透明度和冲击强度的***物理性能平衡。主要特性：FDA，中等粘度和良好的脱模性应用：玩具、食品器具和包装应用 CAS：103598-77-2 信息由 LG 化学提供
LG Chemical Lupoy 1201-10 Polycarbonate Resin 物性表
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 吸水率 | 0.32 % @Temperature 23.0 °C | 0.32 % @Temperature 73.4 °F | equilibrium, 50% RH; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec | 0.15 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | |
| 线性成型收缩率,Flow | 0.00050 - 0.00070 cm/cm | 0.00050 - 0.00070 in/in | ASTM D955 |
| 熔体流动速率 | 10 g/10 min @Load 1.20 kg, Temperature 300 °C | 10 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 洛氏硬度（M 级） | 73 | 73 | ASTM D785 |
| 洛氏硬度（R 级） | 118 | 118 | ASTM D785 |
| 极限抗拉强度 | 72.0 MPa | 10400 psi | ASTM D638 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | 150 % | 150 % | ASTM D638 |
| 屈服伸长率 | 6.0 % | 6.0 % | ASTM D638 |
| 拉伸模量 | 2.41 GPa | 350 ksi | ASTM D638 |
| 弯曲强度 | 96.0 MPa | 13900 psi | ASTM D790 |
| 弯曲模量 | 2.41 GPa | 350 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 9.074 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 17.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | 0.25 mm notch; ASTM D256 |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256 |
| 落锤总能量 | 87.0 J @Thickness 3.20 mm | 64.2 ft-lb @Thickness 0.126 in | 203m/min; ASTM D3763 |
| 磨损 | 45 @Load 1.00 kg | 45 @Load 2.20 lb | [%], CS-10 F wheel, 500 cycles; ASTM D1044 |
| 体积电阻率 | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| 介电常数 | 3.0 @Frequency 60.0 Hz | 3.0 @Frequency 60.0 Hz | ASTM D150 |
| 介电强度 | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| 耗散因数 | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 |
| 相比耐漏电起痕指数(CTI) | 250 V @Thickness 2.00 mm | 250 V @Thickness 0.0787 in | IEC 112 |
| 线性热膨胀系数 | 68.0 m/m-°C @Temperature -40.0 - 82.0 °C | 37.8 in/in-°F @Temperature -40.0 - 180 °F | ASTM D696 |
| Hot Ball Pressure Test | >= 125 °C | >= 257 °F | IEC 598-1 |
| 载荷下热变形温度(0.46 MPa) | 144 °C @Thickness 4.00 mm | 291 °F @Thickness 0.157 in | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 4.00 mm | 262 °F @Thickness 0.157 in | Unannealed; ASTM D648 |
| 141 °C @Thickness 4.00 mm | 286 °F @Thickness 0.157 in | Annealed; ASTM D648 | |
| 维卡软化温度 | 149 °C @Load 5.10 kg | 300 °F @Load 11.2 lb | 50°C/hr; ASTM D1525 |
| 软化温度 | 150 - 200 °C | 302 - 392 °F | melting point per MSDS |
| 可燃性(UL94) | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ASTM D635 |
| V-2 @Thickness 0.500 mm | V-2 @Thickness 0.0197 in | ASTM D635 | |
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ASTM D635 | |
| V-2 @Thickness 2.50 - 2.70 mm | V-2 @Thickness 0.0984 - 0.106 in | ASTM D635 | |
| Flash Point | >= 450 °C | >= 842 °F | |
| 极限氧指数 | 26 % | 26 % | ASTM D2863 |
| 灼热丝试验 | 850 °C @Thickness 2.00 mm, Time 5.00 sec | 1560 °F @Thickness 0.0787 in, Time 0.00139 hour | IEC 695-2-1 |