物性信息:
比重 | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 |
熔体流动速率 | 17.7 g/10 min | 17.7 g/10 min | ASTM D3307 |
肖氏硬度 (邵氏 D) | 60 | 60 | ASTM D2240 |
极限抗拉强度 | 14.0 MPa | 2030 psi | ASTM D3307 |
伸长率 (断裂) | 100 % | 100 % | ASTM D3307 |
悬壁梁缺口冲击强度 | NB | NB | ASTM D256 |
体积电阻率 | 5.0 - 10 ohm-cm | 5.0 - 10 ohm-cm | ASTM D257 |
耐电弧性 | >= 180 sec | >= 180 sec | ASTM D495 |
熔融温度 | 310 - 320 °C | 590 - 608 °F | ASTM D3418 |
最高工作温度, Air | 260 °C | 500 °F | |
可燃性(UL94) | V-0 | V-0 |
加工温度 | 379 - 399 °C | 714 - 750 °F | Cure Temperature |
Heat of Combustion J/g | 5300 | ASTM D240 |