PA6T美国杜邦HTNFR52G30NHDuPont Performance Polymers Zytel® HTN FR52G30NH BK337 Polyphthalamide (PPA) (Unverified Data**)

Polyphthalamide (PPA), 30% Glass Fiber Reinforced

DuPont Performance Polymers

产品说明：

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide

Zytel HTNFR52G30NH BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated fla

Information provided by DuPont Performance Polymers

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法
密度1.44 g/cc0.0520 lb/in³DAM; ISO 1183
线性成型收缩率,Flow0.0030 cm/cm0.0030 in/inDAM; ISO 294-4 2577
线性成型收缩率，横向0.010 cm/cm0.010 in/inDAM; ISO 294-4 2577
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(断裂)150 MPa21800 psiDAM; ISO 527-1/-2
抗张强度0.150 MPa

@Strain 0.000 %, Temperature 175 °C

21.8 psi

@Strain 0.000 %, Temperature 347 °F

DAM; ISO 11403-1 -2

0.180 MPa

@Strain 0.000 %, Temperature 150 °C

26.1 psi

@Strain 0.000 %, Temperature 302 °F

DAM; ISO 11403-1 -2

10.49 MPa

@Strain 0.200 %, Temperature 150 °C

1521 psi

@Strain 0.200 %, Temperature 302 °F

50%RH; ISO 11403-1 -2

12.22 MPa

@Strain 0.110 %, Temperature 40.0 °C

1772 psi

@Strain 0.110 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

13.56 MPa

@Strain 0.110 %, Temperature 23.0 °C

1967 psi

@Strain 0.110 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

13.67 MPa

@Strain 0.110 %, Temperature -40.0 °C

1983 psi

@Strain 0.110 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2

15.62 MPa

@Strain 0.130 %, Temperature 23.0 °C

2265 psi

@Strain 0.130 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2

18.0 MPa

@Strain 0.150 %, Temperature -40.0 °C

2610 psi

@Strain 0.150 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2

30.39 MPa

@Strain 0.760 %, Temperature 175 °C

4408 psi

@Strain 0.760 %, Temperature 347 °F

DAM; ISO 11403-1 -2

33.24 MPa

@Strain 0.680 %, Temperature 150 °C

4821 psi

@Strain 0.680 %, Temperature 302 °F

DAM; ISO 11403-1 -2

33.35 MPa

@Strain 0.830 %, Temperature 150 °C

4837 psi

@Strain 0.830 %, Temperature 302 °F

50%RH; ISO 11403-1 -2

44.64 MPa

@Strain 0.450 %, Temperature 40.0 °C

6474 psi

@Strain 0.450 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

45.48 MPa

@Strain 1.46 %, Temperature 175 °C

6596 psi

@Strain 1.46 %, Temperature 347 °F

DAM; ISO 11403-1 -2

47.11 MPa

@Strain 1.49 %, Temperature 150 °C

6833 psi

@Strain 1.49 %, Temperature 302 °F

50%RH; ISO 11403-1 -2

47.7 MPa

@Strain 0.420 %, Temperature 23.0 °C

6920 psi

@Strain 0.420 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2

48.18 MPa

@Strain 0.440 %, Temperature 23.0 °C

6988 psi

@Strain 0.440 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

49.15 MPa

@Strain 1.26 %, Temperature 150 °C

7129 psi

@Strain 1.26 %, Temperature 302 °F

DAM; ISO 11403-1 -2

55.18 MPa

@Strain 2.30 %, Temperature 175 °C

8003 psi

@Strain 2.30 %, Temperature 347 °F

DAM; ISO 11403-1 -2

55.38 MPa

@Strain 2.19 %, Temperature 150 °C

8032 psi

@Strain 2.19 %, Temperature 302 °F

50%RH; ISO 11403-1 -2

56.61 MPa

@Strain 0.490 %, Temperature -40.0 °C

8211 psi

@Strain 0.490 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2

61.01 MPa

@Strain 1.99 %, Temperature 150 °C

8849 psi

@Strain 1.99 %, Temperature 302 °F

DAM; ISO 11403-1 -2

61.84 MPa

@Strain 0.550 %, Temperature -40.0 °C

8969 psi

@Strain 0.550 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2

64.29 MPa

@Strain 4.64 %, Temperature 150 °C

9324 psi

@Strain 4.64 %, Temperature 302 °F

50%RH; ISO 11403-1 -2

66.07 MPa

@Strain 5.37 %, Temperature 175 °C

9583 psi

@Strain 5.37 %, Temperature 347 °F

DAM; ISO 11403-1 -2

67.98 MPa

@Strain 0.760 %, Temperature 40.0 °C

9860 psi

@Strain 0.760 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

71.24 MPa

@Strain 0.660 %, Temperature 23.0 °C

10330 psi

@Strain 0.660 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2

74.37 MPa

@Strain 4.87 %, Temperature 150 °C

10790 psi

@Strain 4.87 %, Temperature 302 °F

DAM; ISO 11403-1 -2

74.82 MPa

@Strain 0.740 %, Temperature 23.0 °C

10850 psi

@Strain 0.740 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

85.4 MPa

@Strain 1.06 %, Temperature 40.0 °C

12400 psi

@Strain 1.06 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

90.43 MPa

@Strain 0.830 %, Temperature -40.0 °C

13120 psi

@Strain 0.830 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2

91.62 MPa

@Strain 0.860 %, Temperature -40.0 °C

13290 psi

@Strain 0.860 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2

93.25 MPa

@Strain 1.00 %, Temperature 23.0 °C

13520 psi

@Strain 1.00 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

95.43 MPa

@Strain 0.950 %, Temperature 23.0 °C

13840 psi

@Strain 0.950 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2

116.94 MPa

@Strain 1.15 %, Temperature -40.0 °C

16961 psi

@Strain 1.15 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2

118.43 MPa

@Strain 2.11 %, Temperature 40.0 °C

17177 psi

@Strain 2.11 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

119.69 MPa

@Strain 1.18 %, Temperature -40.0 °C

17360 psi

@Strain 1.18 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2

135.95 MPa

@Strain 1.94 %, Temperature 23.0 °C

19718 psi

@Strain 1.94 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

156.87 MPa

@Strain 2.06 %, Temperature 23.0 °C

22752 psi

@Strain 2.06 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2

178.43 MPa

@Strain 2.12 %, Temperature -40.0 °C

25879 psi

@Strain 2.12 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2

196.69 MPa

@Strain 2.46 %, Temperature -40.0 °C

28528 psi

@Strain 2.46 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
伸长率 (断裂)2.2 %2.2 %DAM; ISO 527-1/-2
拉伸模量10.0 GPa1450 ksiDAM; ISO 527-1/-2
弯曲强度230 MPa33400 psiDAM; ISO 178
弯曲模量8.70 GPa1260 ksiDAM; ISO 178
割线模量2.27 GPa

@Strain 3.27 %, Temperature 100 °C

329 ksi

@Strain 3.27 %, Temperature 212 °F

50%RH; ISO 11403-1 -2

3.04 GPa

@Strain 2.27 %, Temperature 100 °C

441 ksi

@Strain 2.27 %, Temperature 212 °F

50%RH; ISO 11403-1 -2

3.38 GPa

@Strain 2.84 %, Temperature 100 °C

491 ksi

@Strain 2.84 %, Temperature 212 °F

DAM; ISO 11403-1 -2

3.90 GPa

@Strain 1.47 %, Temperature 100 °C

565 ksi

@Strain 1.47 %, Temperature 212 °F

50%RH; ISO 11403-1 -2

4.38 GPa

@Strain 1.95 %, Temperature 100 °C

636 ksi

@Strain 1.95 %, Temperature 212 °F

DAM; ISO 11403-1 -2

5.2029 GPa

@Strain 0.690 %, Temperature 100 °C

754.63 ksi

@Strain 0.690 %, Temperature 212 °F

50%RH; ISO 11403-1 -2

5.36 GPa

@Strain 1.24 %, Temperature 100 °C

777 ksi

@Strain 1.24 %, Temperature 212 °F

DAM; ISO 11403-1 -2

5.55 GPa

@Strain 2.07 %, Temperature 80.0 °C

804 ksi

@Strain 2.07 %, Temperature 176 °F

DAM; ISO 11403-1 -2

6.46 GPa

@Strain 1.73 %, Temperature 40.0 °C

937 ksi

@Strain 1.73 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

6.56 GPa

@Strain 0.660 %, Temperature 100 °C

951 ksi

@Strain 0.660 %, Temperature 212 °F

DAM; ISO 11403-1 -2

6.68 GPa

@Strain 0.120 %, Temperature 100 °C

969 ksi

@Strain 0.120 %, Temperature 212 °F

50%RH; ISO 11403-1 -2

6.70 GPa

@Strain 1.46 %, Temperature 80.0 °C

971 ksi

@Strain 1.46 %, Temperature 176 °F

DAM; ISO 11403-1 -2

7.4937 GPa

@Strain 1.27 %, Temperature 40.0 °C

1086.9 ksi

@Strain 1.27 %, Temperature 104 °F

50%RH; ISO 11403-1 -2

7.88 GPa

@Strain 1.57 %, Temperature 23.0 °C

1140 ksi

@Strain 1.57 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2

7.90 GPa

@Strain 0.950 %, Temperature 80.0 °C

1150 ksi

@Strain 0.950 %, Temperature 176 °F

DAM; ISO 11403-1 -2

8.07 GPa

@Strain 0.180 %, Temperature 100 °C

1170 k