本产品引入了高分散体系、超微粉体系、纳米粉体促烧剂等技术,其具有如下优势: (1) 环保:无任何有毒物质的引入; (2) 自流性好:在常温与高温下(~1100℃)流淌性好,其流动值大于240mm; (3) 快速烧结:<30min; (4) 高熔点:采用了超微粉技术促进烧结,其料的熔点更高,耐冲刷和耐侵蚀性能更优越; (5) 高寿命:是传统沥青结合的3倍以上。 |
This product introduces technologies such as high dispersion system, ultra-micro powder system and nanometer powder as catalyst. It has the following advantages:
(1) environmental protection: no introduction of toxic substances;
(2) good self-current : good flow in the normal temperature and high temperature (~1100 ℃) and the flow rate is more than 240 mm;
(3) rapid sintering: <30min;
(4) high melting point: ultra-fine powder technology is adopted to promote sintering. The melting point of the material is higher ,the erosion resistance and erosion resistance are superior.
(5) long service life: 3 times longer than traditional asphalt –combined mass .
产品牌号Brand | CX-CWR | ||
MgO /% ≥ | 85 | ||
SiO2 /% ≤ | 12 | ||
体积密度Bulk density / g. cm-3 ≥ | 1100℃×3h | 2.8 | |
1550℃×3h | 2.7 | ||
耐压强度 Crushing cold strength /MPa ≥ | 25 | 50 | |
抗折强度 Modulus of rupture /MPa ≥ | 1100℃×24h | 8 | 10 |
在转炉内烧结时间 /min ≤ | 30 | ||
常温流动值 / mm ≥ | 240 |