POM日本宝理M25-44 UL黄卡物理性能表
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.41 | g/cm3 | ISO 1183 |
熔流率 (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (190°C/2.16 kg) | 2.20 | cm3/10min | ISO 1133 |
吸水率 (23°C, 24 hr) | 0.50 | % | ISO 62 |
硬度 | 额定值 | ||
洛氏硬度 (M 计秤) | 80 | ISO 2039-2 |
机械性能 | 额定值 | ||
拉伸模量 | 2500 | MPa | ISO 527-2 |
拉伸应力 | 59.0 | ISO 527-2 | |
断张率 | 40 | ISO 527-2 | |
弯曲模量 | 2350 | ISO 178 | |
弯曲强度 | 81.0 | ISO 178 | |
摩擦系数 | JIS K7218 | ||
Dynamic 3 | 0.37 | ||
与钢 - 动态 4 | 0.40 | ||
Wear Factor | JIS K7218 | ||
0.98 MPa, 0.30 m/sec 5 | < 1.0 | 10^-8 mm3/N·m | |
0.98 MPa, 0.30 m/sec 6 | 30 | ||
冲击性能 | 额定值 | ||
简支梁缺口冲击强度 | 8.0 | kJ/m2 | ISO 179/1eA |
热性能 | 额定值 | ||
热变形温度 (1.8 MPa, 未退火) | 90.0 | °C | ISO 75-2/A |
线形膨胀系数 | 内部方法 | ||
流动 : 23 到 55°C | 1.2E-4 | cm/cm/°C | |
横向 : 23 到 55°C |
电气性能 | 额定值 | ||
表面电阻率 | 1.0E+16 | ohm | IEC 60093 |
体积电阻率 | 1.0E+14 | ohm·cm | IEC 60093 |
耐电强度 (3.00 mm) | 19 | kV/mm | IEC 60243-1 |
可燃性 | 额定值 | ||
UL 阻燃等级 | HB | UL 94 |
POM日本宝理M25-44特性
长时间、较宽的温度范围内,能保持拉伸强度、拉伸率及冲击强度等各种机械特性的平衡。
在较宽的温度范围内和长时间受负载的条件下,显示出优良的耐蠕变性能。
具有优良的耐疲劳性,即使是在重复应力或连续振动的条件下,也不会发生疲劳破坏,仍然保持着较安定的性能。
具有高刚性及优良的弹性恢复性能,再加上良好的耐疲劳性和耐蠕变性,作为弹簧材料被广泛应用。
耐磨耗性为热塑性塑料之,同时它还具有良好的润滑性。此外,材料本身也具有自润滑性,适用于不可使用润滑油的部件。
不仅具有良好的短期热性(如熔点、热变形温度等),即使在高温空气及高温热水中长期使用,亦可呈现出良好的性能。
由于吸水引起尺寸变化的可能性很小,故在实际应用几乎不成为问题。
除强酸、强氧化剂的化学药品外,对无机化学药品、油类具有良好的耐化学性。
具有良好的流动性及漂亮的外观,是极易成型的材料。
它既可以嵌入成型,也可以嵌出成型。此外还可以进行切削加工、熔接、印刷等二次加工
In a long time and wide temperature range, it can maintain the balance of various mechanical properties such as tensile strength, tensile rate and impact strength.
It shows excellent creep resistance in a wide temperature range and under long-term load conditions.
It has excellent fatigue resistance. Even under the condition of repeated stress or continuous vibration, fatigue damage will not occur, and it still maintains relatively stable performance.
With high rigidity and excellent elastic recovery performance, plus good fatigue resistance and creep resistance, it is widely used as spring material.
Wear-resistance is one of the thermoplastics, and it also has good lubricity. In addition, the material itself has self-lubrication, which is applicable to parts that cannot use lubricating oil.
It not only has good short-term thermal properties (such as melting point, thermal deformation temperature, etc.), but also shows good performance even if it is used in high-temperature air and high-temperature hot water for a long time.
Because the possibility of size change caused by water absorption is very small, it hardly becomes a problem in practical application.
In addition to strong acid and strong oxidant chemicals, it has good chemical resistance to inorganic chemicals and oils.
With good fluidity and beautiful appearance, it is a very easy to form material.
It can be either embedded or embedded. In addition, it can also carry out secondary processing such as cutting, welding and printing