Solvay Specialty Polymers Hyflon® PFA P450 Perfluoroalkoxy (PFA)

PFA

Solvay Specialty Polymers

产品说明:

Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, inherent flame resistance, low surface energy, and exceptional dielectric properties. Hyflon® PFA resins have been designed to retain their properties over a wide range of temperatures from cryogenic to 250-260°C (482-500°F) and are the material of choice in applications such as linings in the Chemical Process Industry, specialty cables, semiconductor industry, aerospace, and other challenging industries. Hyflon® PFA P450 is a medium molecular weight, high melt flow rate multi purpose resin designed for cable extrusion and injection molding. Hyflon® PFA P450 has obtained UL758 recognition for continuous use at 260°C (500°F) and is an ASTM D3307 - Type I resin.

Features: Flame Retardant; High Flow; High Heat Resistance; Medium Molecular Weight; Semi Crystalline

Uses: Aerospace Applications; Cable Jacketing; Liners; Semiconductor Molding Compounds

Additional Properties: Crystallization Heat - DSC 25.0 to 35.0 J/g; Flex Life - ASTM D2176 (300.0 µm): 4.0E+3 to 6.0E+3 Cycles; Heat of Fusion - DSC 25.0 to 35.0 J/g

Information provided by Solvay Specialty Polymers.

物性信息:

物理性能额定值 (公制)额定值 (英制)测试方法
密度2.13 - 2.18 g/cc0.0770 - 0.0788 lb/in³ASTM D792
熔体流动速率10 - 17 g/10 min

@Load 5.00 kg, Temperature 372 °C

10 - 17 g/10 min

@Load 11.0 lb, Temperature 702 °F

ASTM D1238
机械性能额定值 (公制)额定值 (英制)测试方法
肖氏硬度 (邵氏 D)55 - 6055 - 60ASTM D2240
抗张强度(断裂)>= 21.0 MPa>= 3050 psiASTM D638
伸长率 (断裂)>= 280 %>= 280 %ASTM D638
拉伸模量0.500 - 0.600 GPa72.5 - 87.0 ksi1.0 mm/min; ASTM D638
悬壁梁缺口冲击强度NBNBASTM D256
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率>= 1.00e+17 ohm-cm>= 1.00e+17 ohm-cmASTM D257
表面电阻>= 1.00e+17 ohm>= 1.00e+17 ohmASTM D257
介电常数2.1

@Frequency 100000 Hz

2.1

@Frequency 100000 Hz

ASTM D150

2.1

@Frequency 50.0 Hz

2.1

@Frequency 50.0 Hz

ASTM D150
介电强度35.0 - 40.0 kV/mm889 - 1020 kV/inASTM D149
耗散因数<= 0.00050

@Frequency 100000 Hz

<= 0.00050

@Frequency 100000 Hz

ASTM D150

<= 0.00050

@Frequency 50.0 Hz

<= 0.00050

@Frequency 50.0 Hz

ASTM D150
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动120 - 200 µm/m-°C66.7 - 111 µin/in-°F
比热容0.900 - 1.10 J/g-°C0.215 - 0.263 BTU/lb-°FASTM C351
导热系数0.200 W/m-K

@Temperature 40.0 °C

1.39 BTU-in/hr-ft²-°F

@Temperature 104 °F

ASTM C177
熔融温度300 - 310 °C572 - 590 °FDSC
Crystallization Temperature275 - 285 °C527 - 545 °FPeak; ASTM D3418
高工作温度, Air260 °C500 °FContinuous Use
可燃性(UL94)V-0V-0
极限氧指数95 %95 %ASTM D2863

材料描述
测试方法
机构评级ASTM D 3307 Type I; UL 758
可用性Africa & Middle East

Asia Pacific

Europe

Latin America

North America
形式Pellets
加工技术Extrusion; Injection Molding

高温电线、电缆绝缘层,防腐设备、密封材料、泵阀衬套,和化学容器。

成型性能 1.结晶料,吸湿小。可采用通常得热塑性塑料得加工方法加工成制品。

3、流动性差,极易分解,分解时产生腐蚀气体。宜严格控制成型温度不要超过475度,模具应加热至150-200度,浇注系统对料流阻力应小。

4、半透明粒料,注塑、挤出成型。成型温度350-400度,475度以上容易引起变色或发生气泡。并注意脱模会较困难。

5、因熔融的材料对金属有腐蚀作用,长期生产,模具需要电镀铬处理。

PFA FEP PTFE 的化学性能相似,但FEP只能在200度以下使用,PTFE不能注塑。