MATERIAL | SPECIFIC RESISTANCE (Ω–CM/F) | MELTING POINT °C | COMPOSITION | |
Aluminum | ||||
1 | ALUMINUM 1% SILICON | 15.2 | 657 | |
2 | ALUMINUM 1199 | 15.97 | 660 | Al99.99% |
3 | ALUMINUM EC 1350 | 16.83 | 657 | Al99.45% |
4 | ALUMINUM 2024 | 20.25 | 638 | Al93.84%Cu4.5%Mg1.5%Mn0.16% |
5 | ALUMINUM 3003 | 20.25 | 634 | Al98.8%Mn1.2% |
6 | ALUMINUM 4043 | 25 | 632 | Al94.75%Si5.25% |
7 | ALUMINUM 5005 | 19.95 | 652 | Al99.2%Mn0.8% |
8 | ALUMINUM 5052 | 10.23 | 649 | Al97.25%Cr0.25%Mn2.5% |
9 | ALUMINUM 5056 | 35.79 | 638 | Al94.6%Cr0.1%Mg0.1%Mn0.1% |
10 | ALUMINUM 6061 | 23.04 | 649 | Al97.9%Cr0.25%Cu0.25%Mg1%Si0.6% |
Copper | ||||
1 | ALLOY 725 | 94.3 | 1060 | Cu88.2%Ni9.5%Sn2.3% |
2 | BE COPPER ALLOY 10 CDA 175 | 22.8 | 1029 | Be0.55%Co2.55%Cu96.9% |
3 | BE COPPER ALLOY 25 CDA 172 | 46.2 | 865 | Be1.8%Cu98.1% |
4 | BE COPPER CDA 17410 | 36.9 | 1025 | Be0.3%Co0.5%Cu99% |
5 | BRASS FREE-CUT CDA 360 | 39.9 | 885 | Cu61.5%Pb3.1%Zn35.4% |
6 | BRASS 7030 CDA 230 | 37 | 915 | Cu70%Zn30% |
7 | BRASS GILDING CDA 210 | 18.5 | 1050 | Cu95%Zn5% |
8 | CADMIUM COPPER CDA 162 | 11.5 | 1030 | Cd1%Cu99% |
9 | COMMERCIAL BRonZE 90% CDA 220 | 23.6 | Cu90%Zn10% | |
10 | COPPER 27% NICKEL CLAD | 14 | 1100 | Cu99.9%Ni99% |
11 | COPPER 99.95% CDA 102 OF | 10.3 | 1083 | Cu99.5%min |
12 | COPPER 99.99% CDA 101 | 10.3 | 1083 | Cu99.99%min |
13 | COPPER ETP MAGNET WIRE | 10.3 | Cu99.9%min | |
14 | COPPER NICKEL 20% | 160 | 1150 | Cu79%Ni21% |
15 | COPPER ZIRConIUM CDA 150 | 11.2 | 980 | Cu99.85%Zr0.15% |
16 | CUPRO NICKEL 70-30 | 225 | 1170 | Cu69.5%Fe0.5%Ni30% |
17 | LOW BRASS CDA 240 | 32.4 | 965 | Cu80%Zn20% |
18 | NICKEL SILVER CDA 752 | 173 | 1070 | Cu65%Ni18%Zn17% |
19 | NICKEL SILVER CDA 757 | 130 | 1040 | Cu65%Ni12%Zn23% |
20 | NICKEL SILVER CDA 764 | 189 | 1020 | Cu60%Ni18%Zn22% |
21 | PD-135 | 11.3 | 1080 | Cd1%maxCr1%maxCu99%min |
22 | PH BRonZE 5% CDA 510 A | 69.1 | 950 | Cu94.8%P0.2%Sn5% |
23 | PH BRonZE 8% CDA 521 C | 79.8 | 880 | Cu92%P0.16%Sn8% |
24 | PH BRonZE 10% CDA 524 D | 94.3 | 845 | Cu90%Sn10% |
Nickel | ||||
1 | ALLOY 99 | 48 | 1450 | Ni99.8%min |
2 | DURANICKEL 301 | 255 | 1450 | Al4%-4.75%Ni93%Ti0.25%-1% |
3 | MonEL 400 | 290 | 1350 | Cu32.5%Fe2.5%Mn2%Ni63% |
4 | MonEL 404 | 319 | 1299 | Cu43%-48%Ni52%-57% |
5 | Monel K 500 | 370 | Al2.3%-****%Cu23.35%-34.5%Fe2%maxMn1.5%maxNi63%-70% | |
6 | NICKEL 205 | 50 | 1450 | Ni99.45%min |
7 | NICKEL 211 | 102 | 1430 | Mn4.75%Ni93.7% |
8 | NICKEL 220 | 45 | 1450 | |
9 | NICKEL 270 | 45 | 1450 | Ni99.97%min |
10 | NICKEL A/200 | 48 | 1450 | Ni99%min |
Precious metal | ||||
1 | ALLOY 20-245 | 245 | ||
2 | ALLOY 406 | 75 | ||
3 | ALLOY 411 | 37.0009 | Ag89%Pd11% | |
4 | ALLOY 417 | 57 | ||
5 | ALLOY 422 | 180 | 1880 | |
6 | ALLOY 443 | 80 | ||
7 | ALLOY 446 | 190 | ||
8 | ALLOY 486 | 610 | 1700 | |
9 | GOLD 99.99% BE MOD | 12.6 | 1063 | Au99.99%min |
10 | GOLD 99.99% | 14.14 | 1063 | Au99.99%min |
11 | PALLADIUM | 60 | 1554 | Pd99%min |
12 | PLATINUM 8% TUNGSTEN | 400 | 1870 | Pt92%W8% |
13 | PLATINUM 10% IRIDIUM | 150 | 1775 | Ir10%Pt90% |
14 | PLATINUM 10% RHODIUM | 111 | 1850 | Pt90%Rh10% |
15 | PLATINUM 20% IRIDIUM | 186 | 1840 | Ir20%Pt80% |
16 | PLATINUM 20% RHODIUM | 125 | 1900 | Pt80%Rh20% |
17 | PLATINUM PURE TC GRADE | 64 | 1773 | Pt99.99%min |
18 | RHODIUM 99.8% | 30 | 1960 | Rh99.8%min |
19 | SILVER 99.99% | 8.8 | 960 | Ag99.99% |
Resistance Wire | ||||
1 | MANGANIN 230 SHUNT | 230 | 1020 | Cu84%Mn12%Ni4% |
2 | MANGANIN 290 | 290 | 1020 | Cu84%Mn12%Ni4% |
3 | NICKEL ALLOY 30 | 30 | 1100 | Cu98%Ni4% |
4 | NICKEL ALLOY 60 | 60 | 1100 | Cu94%Ni6% |
5 | NICKEL ALLOY 90 | 90 | 1100 | Cu90%Ni10% |
6 | NICKEL ALLOY 120 | 120 | 1425 | Fe30%Ni70% |
7 | NICKEL ALLOY 180 | 180 | 1100 | Cu78%Ni22% |
8 | NICO | 294 | 1210 | Cu55%Ni45% |
9 | NIFE 5200 | 120 | 1425 | Fe30%Ni70% |
10 | STABLOHM 610 (TOPHET D) | 610 | 1300 | Cr20%Fe45%Ni35% |
11 | STABLOHM 650 | 650 | 1395 | Cr20%Ni80%Si1%-2% |
12 | STABLOHM 675 | 675 | 1350 | Cr16%Fe34%Ni60% |
13 | STABLOHM 710 | 710 | 1377 | Cr30%Ni70% |
14 | STABLOHM 750 | 750 | 1510 | Al4%Cr15%Fe81% |
15 | STABLOHM 800 A | 800 | 1395 | Al2.5%Cr20%Cu2.5%Ni75% |
16 | STABLOHM 812 | 812 | 1510 | Al4.5%Cr21%Fe74.5% |
17 | STABLOHM 875 | 875 | 1520 | Al5.5%Cr22.5%Fe72% |
Stainless Steel | ||||
1 | STAINLESS STEEL 302 | 420 | 1399 | |
2 | STAINLESS STEEL 304 | 420 | 1399 | |
3 | STAINLESS STEEL 305 | 420 | 1399 | |
4 | STAINLESS STEEL 308 | 455 | 1399 | |
5 | STAINLESS STEEL 309 | 170 | 1399 | |
6 | STAINLESS STEEL 310 | 520 | 1399 | |
7 | STAINLESS STEEL 316 | 470 | 1371 | |
8 | STAINLESS STEEL 316L | 445 | 1399 | |
9 | STAINLESS STEEL 347 | 470 | 1399 | |
10 | STAINLESS STEEL 430 | 360 | 1427 | |