注塑PA66 101L | ||||
产品参数 | ||||
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM|50%RH,1.2|- | % |
吸水率 | 饱和(23℃) | ASTM D-570 | DAM|50%RH,8.5|- | % |
比重 | ASTM D-792 | DAM|50%RH,1.14|1.14 | ||
泰伯磨耗量 | cs-17 Wheel 1000g | DAM|50%RH,-|7 | mg/1000 cycles | |
埃佐冲击强度 | 23℃ | ASTM D-256 | DAM|50%RH,53|112 | j/m |
洛氏硬度M | ASTM D-785 | DAM|50%RH,M79|M59 | ||
硬度计硬度 | ASTM D-676 | DAM|50%RH,89|82 | ||
洛氏硬度R | ASTM D-785 | DAM|50%RH,R121|R108 | ||
屈服强度 | 23℃ | DAM|50%RH,82.7|58.6 | MPa | |
拉伸强度 | 23℃ | ASTM D-638 | DAM|50%RH,82.7|77.2 | MPa |
揉曲模量 | 23℃ | ASTM D-790 | DAM|50%RH,2827|1207 | MPa |
拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM|50%RH,157|231 | KJ/m2 |
1%形变时的压应力 | ASTM D-695 | DAM|50%RH,33.8|- | MPa | |
剪切强度 | 23℃ | ASTM D-732 | DAM|50%RH,66.2|- | MPa |
断裂伸长率 | 23℃ | ASTM D-638 | DAM|50%RH,60|≥300 | % |
屈服伸长率 | ASTM D-638 | DAM|50%RH,5|25 | % | |
拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM|50%RH,504|1470 | KJ/m2 |
介电常数 | 106Hz(cps) | ASTM D-150 | DAM|50%RH,3.6|4.6 | |
耗散因数 | 100Hz(cps) | ASTM D-150 | DAM|50%RH,0.01|0.2 | |
介电常数 | 103Hz(cps) | ASTM D-150 | DAM|50%RH,3.9|7.0 | |
耗散因数 | 106Hz(cps) | ASTM D-150 | DAM|50%RH,0.02|0.1 | |
耗散因数 | 103Hz(cps) | ASTM D-150 | DAM|50%RH,0.02|0.2 | |
体积电阻率 | ASTM D-257 | DAM|50%RH,10,15,|10,13 | Ω.cm | |
介电常数 | 100Hz(cps) | ASTM D-150 | DAM|50%RH,4.0|8.0 | |
荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM|50%RH,1.4|- | % |
热畸变温度 | 18×106Pa | ASTM D-648 | DAM|50%RH,90|- | ℃ |
熔点结晶 | ASTM D-2177 | DAM|50%RH,270|- | ℃ | |
UL可燃性导级 | UL 94 | DAM|50%RH,94|V-2 | ||
脆化温度 | ASTM D-746 | DAM|50%RH,-80|-65 | ℃ | |
热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM|50%RH,235|- | ℃ |
导热系数 | DAM|50%RH,0.25|- | w/mk | ||
线性热膨胀系数 | ASTM D-696 | DAM|50%RH,7×10,-5,|- | m/m/℃ | |
熔点 | Fisher Johns法 | ASTM D-789 | DAM|50%RH,255|255 | ℃ |
需氧指数 | ASTM D-2863 | DAM|50%RH,28|31 | % | |