Adsyl 5 C 37 F
Polyolefin
Lyondellbasell Industries
产品说明：
Adsyl 5 C 37 F is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications.
This grade features a very low seal initiation temperature.
It contains slip and anti-block additives.
For regulatory information please refer to Adsyl 5 C 37 F Product Stewardship Bulletin (PSB).
物性信息：
| 基本信息 |
|
|---|
| 添加剂 | |
| 特性 | |
| 用途 | Bi-axially Oriented Film 薄膜 层压板 流延薄膜 食品包装 收缩性薄膜
|
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.900 | g/cm³ | ASTM D792, ISO 1183/A |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238, ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 (屈服) | 21.4 | MPa | ASTM D638 |
| 伸长率 (屈服) | 13 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 1 | 648 | MPa | ASTM D790A |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 薄膜厚度 - 经测试 | 50 | µm |
|
| 拉伸模量 |
|
| ISO 527-3/25 |
| MD : 50 µm, 铸造薄膜 | 280 | MPa | ISO 527-3/25 |
| TD : 50 µm, 铸造薄膜 | 280 | MPa | ISO 527-3/25 |
| 拉伸应力 |
|
| ISO 527-3/500 |
| MD : 屈服, 50 µm, 铸造薄膜 | 14.0 | MPa | ISO 527-3/500 |
| TD : 屈服, 50 µm, 铸造薄膜 | 14.0 | MPa | ISO 527-3/500 |
| MD : 断裂, 50 µm, 铸造薄膜 | 45.0 | MPa | ISO 527-3/500 |
| TD : 断裂, 50 µm, 铸造薄膜 | 35.0 | MPa | ISO 527-3/500 |
| 伸长率 |
|
| ISO 527-3/500 |
| MD : 屈服, 50 µm, 铸造薄膜 | 17 | % | ISO 527-3/500 |
| TD : 屈服, 50 µm, 铸造薄膜 | 15 | % | ISO 527-3/500 |
| MD : 断裂, 50 µm, 铸造薄膜 | 900 | % | ISO 527-3/500 |
| TD : 断裂, 50 µm, 铸造薄膜 | 800 | % | ISO 527-3/500 |
| 始封温度 | 105 | °C |
|
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 85 | J/m | ASTM D256A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 | 62.8 | °C | ASTM D648 |
| 0.45 MPa, 未退火 | 62.0 | °C | ISO 75-2/B |
| 维卡软化温度 | 107 | °C | ISO 306/A50 |
| 熔融温度 | 132 | °C | ISO 11357-3 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 光泽度 (45°, 50.0 µm, 铸造薄膜) | 87 |
| ASTM D2457 |
| 雾度 (50.0 µm, 铸造薄膜) | 1.0 | % | ASTM D1003 |