牌号
AWS
GB/T 15620
焊丝化学成分(wt.%)
C
Mn
Fe
P
S
Si
Cu
Ni
Al
Ti
Cr
Nb(Cb)+Ta
Mo
其他
ERNi-1
ERNi-1
SNi2061
≤0.15
≤1.0
≤1.0
≤0.03
≤5
≤0.75
≤0.25
≥93.00
≤1.5
2.0-3.5
—
—
—
≤0.50
ERNiCu-7
ERNiCu-7
SNi4060
≤0.15
≤4.0
≤2.5
≤0.02
≤5
≤1.25
余量
62.0-
69.0
≤1.25
1.5-3.0
—
—
—
≤0.50
ERNiCr-3
ERNiCr-3
SNi6082
≤0.10
2.5-3.5
≤3.0
≤0.03
≤5
≤0.50
≤0.50
≥67.0
—
≤0.75
18.0-22.0
2.0-3.0
—
≤0.50
ERNiCr-4
ERNiCr-4
SNi6072
-
0.10
≤0.20
≤0.50
≤0.02
≤5
≤0.20
≤0.50
余量
—
0.3-1.0
42.0-46.0
—
—
≤0.50
ERNiCrFe-7
ERNiCrFe-7
SNi6052
≤0.04
≤1.0
7.0-
11.0
≤0.02
≤5
≤0.50
≤0.30
余量
≤1.10
≤1.0
28.0-31.5
≤0.10
≤0.50
≤0.50
ERNiCrFe-7A
ERNiCrFe-7A
—
≤0.04
≤1.0
7.0-
11.0
≤0.02
≤5
≤0.50
≤0.30
余量
≤1.10
≤1.0
28.0-31.5
0.5-1.0
≤0.50
≤0.50
Co≤0.12
ERNiCrMo-3
ERNiCrMo-3
SNi6625
≤0.10
≤0.50
≤5.0
≤0.02
≤5
≤0.50
≤0.50
≥58.0
≤0.40
≤0.40
20.0-23.0
315-4.15
8.0-
10.0
≤0.50
ERNiCrMo-4
ERNiCrMo-4
SNi6276
≤0.02
≤1.0
4.0-
7.0
≤0.04
≤0.03
≤0.08
≤0.50
余量
Co: ≤2.5
V:≤0.35
14.5-16.5
W: 3.0-4.5
15.0-17.0
≤0.50
ERNiCrMo-10
ERNiCrMo-10
SNi6022
≤5
≤0.50
2.0-
6.0
≤0.02
≤0
≤0.08
≤0.50
余量
Co: ≤2.5
V:≤0.35
20.0-22.5
W: 2.5-4.5
12.5-14.5
≤0.50
ERNiCrMo-13
ERNiCrMo-13
SNi6059
≤0
≤0.50
≤1.50
≤5
≤0.005
≤0.10
—
余量
0.1-0.4
Co: ≤0.3
22.0-24.0
—
15.0-16.5
≤0.50
ERNiFeCr-1
ERNiFeCr-1
SNi8065
≤0.05
≤1.0
≥22.0
≤0.03
≤0.03
≤0.50
1.5-3.0
38.0-
46.0
≤0.20
0.6-1.2
19.5-23.5
—
2.5-
3.5
≤0.50
ERNiFeCr-2
ERNiFeCr-2
SNi7718
≤0.08
≤0.35
余量
≤5
≤5
≤0.35
≤0.30
50.0-
55.0
0.20-
0.80
0.65-1.15
17.0-21.0
4.75-5.50
2.80-3.30
≤0.50
B≤0.006
ERNiCrCoMo-1
ERNiCrCoMo-1
SNi6617
0.05-
0.15
≤1.0
≤3.0
≤0.03
≤5
≤1.0
≤0.50
余量
0.8-1.5
≤0.60
20.0-24.0
Co: 10.0-15.0
8.0-
10.0
≤0.50
ERNiMo-8
ERNiMo-8
SNi1008
≤0.10
≤1.0
≤10.0
≤5
≤5
≤0.50
≤0.50
≥60.0
—
—
0.5-
3.5
W: 2.0-4.0
18.0-21.0
≤0.50
ERNiCrMo-3镍基合金焊丝焊接注意事项:
1、焊接处须彻底清除油污、铁锈、水份等表面杂质。
2、焊接时，采用小线能量，建议采用较低的道间温度。
3、所使用的氩气的纯度要在99.99%以上且气体的流量控制要适当，通常焊接电流在100-200A时，气体流量约为10-15L/min。
4、施焊时必须有适当的防风设施，否则保护气体易受风的影响而致气体保护不良。使焊道劣化而发生气孔。
5、适当选择喷嘴及控制钨电的恰当伸岀长度。