| 熔体流动速率 | 32 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 降伏点抗张强度 | 280 | kg/cm | ASTM D-638 |
| IZOD缺口冲击强度 (23℃) | 9 | kg.cm/cm | ASTM D-256 |
| IZOD冲击强度 (-20℃) | 4 | kg.cm/cm | ASTM D-256 |
| 断裂伸长率 | 5 | % | ASTM D-638 |
| 洛氏硬度 | 98 | R标尺 | ASTM D-785 |
| 弯曲模量 | 16000 | kg/cm | ASTM D-790 |
| 熔体流动速率 | 32 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 降伏点抗张强度 | 280 | kg/cm | ASTM D-638 |
| IZOD缺口冲击强度 (23℃) | 9 | kg.cm/cm | ASTM D-256 |
| IZOD冲击强度 (-20℃) | 4 | kg.cm/cm | ASTM D-256 |
| 断裂伸长率 | 5 | % | ASTM D-638 |
| 洛氏硬度 | 98 | R标尺 | ASTM D-785 |
| 弯曲模量 | 16000 | kg/cm | ASTM D-790 |