| 熔体流动速率 | ASTM D-1238(ISO 1133) | ||
| (220℃×10kgf(98N)) | 50 | g/10min | |
| (200℃×5kgf(49N)) | 5.0 | g/10min |
| 比重 (23℃/23℃) | 1.04 | ASTM D-792(ISO 1183) |
| 弯曲模量 (23℃) | 24000(2350) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 弯曲强度 (23℃) | 690(68) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 洛氏硬度 (23℃) | R-104 | ASTM D-785(ISO 2039/2) | |
| 拉伸强度 (23℃) | 410(40) | kg/cm(MPa) | ASTM D-638(ISO 527) |
| IZOD冲击强度 (23℃1/4"厚) | 30(294) | kg.cm/cm(J/m) | ASTM D-256(ISO R180) |
| 燃烧性 (FILE NO E162823) | 1/16"HB All Corlor | UL 94 | |
| 热变形温度 (Annealed(8℃×8hr)) | 100 | ℃ | ASTM D-648(ISO 75/A) |
| 维卡软化点 (1Kg load) | 103 | ℃ | ASTM D-1525(ISO 306) |
| 热变形温度 (Unanneaied 18.6kg/cm²(1/2"厚)) | 88 | ℃ | ASTM D-648(ISO 75/A) |