| 熔体流动速率 (230℃.2.16kg) | 12 | g/10min | ASTM D-1238L |
| 密度 | 0.9 | G/cm | ASTM D-1505 |
| 拉伸屈服强度 | 270 | MPa | ASTM D-638 |
| 断裂伸长率 | 6 | % | ASTM D-638 |
| IZOD冲击强度 (23℃) | 10 | Kg.cm/cm | ASTM D-256 |
| 洛氏硬度 | 95 | R标尺 | ASTM D-785 |
| IZOD冲击强度 (-20℃) | 5 | Kg.cm/cm | ASTM D-256 |
| 弯曲模量 | 11500 | MPa | ASTM D-790 |
| 熔体流动速率 (230℃.2.16kg) | 12 | g/10min | ASTM D-1238L |
| 密度 | 0.9 | G/cm | ASTM D-1505 |
| 拉伸屈服强度 | 270 | MPa | ASTM D-638 |
| 断裂伸长率 | 6 | % | ASTM D-638 |
| IZOD冲击强度 (23℃) | 10 | Kg.cm/cm | ASTM D-256 |
| 洛氏硬度 | 95 | R标尺 | ASTM D-785 |
| IZOD冲击强度 (-20℃) | 5 | Kg.cm/cm | ASTM D-256 |
| 弯曲模量 | 11500 | MPa | ASTM D-790 |