产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 成型收缩率 | ASTM D-955 | 0.9-1.4 | % | |
| 比重 | ASTM D-792 | 1.06 | |||
| 机械性能 | 弯曲模量 | ASTM 790 | 2840 | MPa | |
| Izod缺口冲击强度 | ASTM D-256 | 50 | J/m | ||
| Izod缺口冲击强度 | ASTM D-256 | 5 | Kg.cm/cm | ||
| 弯曲强度 | ASTM D-790 | 7700 | psi | ||
| 弯曲模量 | ASTM D-790 | 29000 | Kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 33 | MPa | ||
| 拉伸屈服强度 | ASTM D-638 | 5300 | psi | ||
| 拉伸屈服强度 | ASTM D-638 | 36 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 20 | % | ||
| 弯曲强度 | ASTM D-790 | 540 | Kg/cm2 | ||
| 拉伸屈服强度 | ASTM D-638 | 370 | Kg/cm2 | ||
| Izod缺口冲击强度 | ASTM D-256 | 0.9 | ft.lb/in | ||
| 弯曲模量 | ASTM D-790 | 410 | psi | ||
| 热性能 | 热变形温度 | 0.45Mpa | ASTM D-648 | 145 | ℃ |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 200 | °F | |
| 热变形温度 | 0.45Mpa | ASTM D-648 | 295 | °F | |
| 耐燃性 | ASTM UL94 | HB | class | ||
| 热变形温度 | 1.82Mpa | ASTM D-648 | 92 | ℃ | |