Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Hostaform® acetal copolymer grade MT8F02 is a special grade developed for medical industry applications containing low residual monomers. Hostaform® MT8F02 is a standard flow high level polytetrafluoroethylene filled (PTFE) product designed for use in wear applications against plastics, metal, glass or ceramic mating surfaces where silicone lubricants can not be tolerated.
物性信息：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 1.52 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| 收缩率 |
|
| ISO 294-4 |
| 垂直流动方向 | 1.7 | % | ISO 294-4 |
| 流动方向 | 2.0 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 0.20 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | 2500 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 48.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 7.0 | % | ISO 527-2/1A/50 |
| 标称拉伸断裂应变 | 16 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 |
|
| ISO 899-1 |
| 1 hr | 2100 | MPa | ISO 899-1 |
| 1000 hr | 1200 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 2400 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 简支梁缺口冲击强度 |
|
| ISO 179/1eA |
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
| -30°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 热变形温度 (1.8 MPa, 未退火) | 98.0 | °C | ISO 75-2/A |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 - 流动 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 注射 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 80.0 到 100 | °C |
|
| 干燥时间 | 3.0 | hr |
|
| 料筒后部温度 | 176 | °C |
|
| 料筒中部温度 | 182 | °C |
|
| 料筒前部温度 | 188 | °C |
|
| 射嘴温度 | 198 | °C |
|
| 加工（熔体）温度 | 180 到 200 | °C |
|
| 模具温度 | 80.0 到 120 | °C |
|
| 注塑压力 | 60.0 到 120 | MPa |
|
| 注射速度 | 慢 |
|
|
| 保压 | 60.0 到 120 | MPa |
|
| 背压 | 0.00 到 0.500 | MPa |
|