| 比重 | 0.900 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (23°C) | 1.4 到 1.8 | % | 内部方法 |
| 洛氏硬度 (R 级, 23°C) | 100 | ASTM D785 |
| 抗张强度 (屈服, 23°C) | 33.3 | MPa | ASTM D638 |
| 伸长率 (断裂, 23°C) | > 200 | % | ASTM D638 |
| 弯曲模量 (23°C) | 1370 | MPa | ASTM D790A |
| 无缺口悬臂梁冲击 (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| 载荷下热变形温度 (0.45 MPa, 未退火, 6.35 mm) | 110 | °C | ASTM D648 |
| UL 阻燃等级 (1.50 mm, All Colors) | HB | UL 94 |