搪瓷管经过高温焙烧、冷却后，搪瓷与钢板就粘结在了一起。由于搪瓷的线膨胀系数和延伸率小于钢板的特性，冷却后搪玻璃的变形量会小于钢板的变形量，而搪瓷受到钢板的约束就会产生压应力。也就是说搪瓷管制成后，搪玻璃会存在一种预压缩应力，搪瓷管空气预热器，而钢板则存在预拉伸应力。
Enamel tube through the high temperature roasting， cooling， enamel and steel te is bonded together. Because the characteristics of enamel of the coefficient of linear expansion and extension rate is less than the te， deformation after cooling glass lining will be less than the amount of deformation of steel， and steel te enamel ctrained will generate compressive stress. That is to say the enamel tube， glass lined there will be a pre compressive stress， and the steel te are pre tensile stress.
由于预应力与线膨胀系数和延伸率相关，而线膨胀系数、延伸率又与温度密切相关，因此搪瓷管的工作温度对瓷管本身的使用会带来很大的影响。在这里需要注意温度的变化，如果温度变化大，很容易使搪瓷产生的应力超过使用应力，从而引起搪瓷的破坏，一旦搪瓷层遇到冷、热急变，搪瓷管预热器，极易发生爆瓷现象。
Due to prestressing force and the coefficient of linear expansion and extension rate，搪瓷管图片， and the coefficient of linear expansion， elongation and closely related with the temperature， so the enamel pipe working temperature on the porcelain tube itself use will have a great impact. Here we need to pay attention to the change of temperature， if the temperature change is big， easy to cause the enamel of stress over the use of stress， so as to cause enamel damage， once the enamel layer encountered cold and hot blast，搪瓷管， prone to burst phenomenon of porcelain.
空气预热器形成腐蚀与积灰的原因
下面小编就为大家介绍一下空气预热器形成腐蚀与积灰的原因，希望对您有所帮助。
由于空气预热器处于锅炉内烟温低区，特别是末级空气预热器的冷端，空气的温度低、烟气温度也低，受热面壁温低，因而容易产生腐蚀和积灰。
当燃用含硫量较高的燃料时，生成的SO2和SO3气体，与烟气中水蒸气生成压硫酸或硫酸蒸汽，在排烟温度低到使受热面壁温低于酸蒸汽时，硫酸蒸汽便会凝结在受热面上，岁金属壁面产生严重腐蚀，称为低温腐蚀。同时，空气预热器除正常积存部分灰分外，酸流体也会粘在烟气中的灰分，越积越多，易产生积灰。因此，受热面的低温腐蚀和积灰是相互促进的。
搪瓷管可以内外都是搪瓷吗？
可以做内外搪瓷，不过这样对搪瓷母管的材质要求很高还有就是搪瓷材料的配比这个要设计到防鳞爆，难度系数比普通单面搪瓷大，一般搪瓷生产厂家都做不了。一般空预器是只用外搪瓷或内搪瓷，内外双面搪瓷的比较少，垃圾焚烧炉用一般是双面搪瓷因为空气中的硫含量相当高，单面搪瓷效果往往不是很好，您的考虑还是比较全的。