物性表
物性纠错
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 模具收缩率 | 3.2mm,flow | ASTM D-792 | DAM｜0.4 | % |
| 3.2mm,flow | ASTM D-792 | 50%RH｜- | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| IZOD缺口冲击强度 | ASTM D-256 | DAM｜100 | J/m | |
| ASTM D-256 | 50%RH｜105 | J/m | ||
| 断裂伸长率 | ASTM D638/ISO 527 | 2.5 | % | |
| 拉伸强度 | ASTM D638/ISO 527 | 169 | kg/cm²(MPa)[Lb/in²] | |
| ASTN D-638 | DAM｜169 | Mpa | ||
| ASTN D-638 | 50%RH｜134 | Mpa | ||
| 伸长率 | 断裂 | ASTM D-638 | DAM｜2.5 | % |
| 断裂 | ASTM D-638 | 50%RH｜4 | % | |
| 弯曲模量 | ASTM D790/ISO 178 | 8960 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D-790 | DAM｜8960 | Mpa | ||
| ASTM D-790 | 50%RH｜6900 | Mpa | ||
| 弯曲强度 | ASTM D790/ISO 178 | 240 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D-790 | DAM｜240 | Mpa | ||
| ASTM D-790 | 50%RH｜- | Mpa | ||
| IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 100 | kg·cm/cm(J/M)ft·lb/in |