物性表
物性纠错
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 收缩率 | 干 | 旭化成方法 | 1.3-2.0 | % |
| MD2.0mm | ASTMD995 | 1.3 | % | |
| TD2.0mm | ASTMD995 | 2.0 | % | |
| 吸水率 | (23°C,24hr) | ASTMD570 | 2.5 | % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 断裂伸长率 | 23°C | ASTMD638 | 50 | % |
| ASTM D638/ISO 527 | 50 | % | ||
| 断裂延伸率 | 干(湿) | ASTM D-638 | 50(250) | % |
| 抗挠强度 | 干(湿) | ASTM D-790 | 118(54) | Mpa |
| 抗挠系数 | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
| 拉伸强度 | 干(湿) | ASTM D-638 | 79(57) | Mpa |
| 23°C | ASTMD638 | 79 | Mpa | |
| 洛氏硬度 | 干(湿) | ASTM D-785 | 120(108) | R scale |
| 干(湿) | ASTM D-785 | 80(55) | M Scale | |
| 磨耗率 | 湿 | ASTM D-1044 | 7 | |
| 弯曲模量 | 23°C | ASTMD790 | 2800 | Mpa |
| ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in | ||
| 弯曲强度 | ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in | |
| 23°C | ASTMD790 | 118 | Mpa | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 39 | J/m |
| 悬臂梁式缺口冲击强度 | 干(湿) | ASTM D-256 | 39(147) | J/m |
| Charpy冲击强度 | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |